Evaluation of the barrier and antimicrobial properties of biodegradable films based on potato waste starch containing natural additives

This study investigates the antimicrobial and water vapor barrier properties of biodegradable films made from potato (Solanum tuberosum) waste starch and the natural additives glycerol, propolis, and montmorillonite ("chaco"). Films were produced using the casting method, and their physical, antimicrobial, and barrier properties were analyzed. Film compositions were established using an experimental design of mixtures. The water vapor permeability values ranged from 0.44 x 10-10 to 8.55 x 10-10 g/(m center dot s center dot Pa). The permeation energy was lower than that of polyvinyl chloride and polypropylene films but higher than that of cellophane films. The solubility values ranged from 58 to 66%, and the tensile modulus ranged from 2.15 to 5.15 MPa. The largest inhibition halo diameter obtained for Staphylococcus aureus was 17 mm. The developed packages completely biodegrade within 30 days under composting conditions at ambient temperatures. These findings suggest the potential application of these biodegradable packages for fresh products such as fruits and vegetables. Biodegradable films containing potato waste starch, glycerol, and natural additives were developed and studied.Peruvian clay "chaco" and propolis affected the barrier and antimicrobial properties of biodegradable packaging.All developed films completely biodegraded in compost within 30 days at ambient conditions.