Study on wettability behavior and wear resistance mechanism of ZTA-ceramic-reinforced HCCI composites

被引：4
|
作者：
Gao, Quan [1 ]
Lv, Zhenlin [1 ]
Jia, Lei [1 ]
Zhang, Chaoyang [1 ]
机构：
[1] Xian Univ Technol, Sch Mat Sci & Engn, 5 South Rd, Xian, Peoples R China
来源：
COMPOSITE INTERFACES | 2023年 / 30卷 / 11期
关键词：
ZTA; HCCI composites; wettability behavior; pressureless sintering; wear resistance; CORROSION BEHAVIOR; MATRIX COMPOSITES; ABRASIVE WEAR; IRON; PARTICLES; LAYER; NI;
D O I：
10.1080/09276440.2023.2210883
中图分类号：
TB33 [复合材料];
学科分类号：
摘要：
Zirconia-toughened alumina (ZTA)-reinforced high-chromium cast iron (HCCI) composite materials were prepared using pressureless sintering method, and the effects of the type (titanium (Ti), nickel (Ni)) and content (10%, 12%) of active additives on the wettability and wear resistance were systematically studied. Result showed that the additive can enhance the wettability capacity between ZTA/HCCI composites interface, especially Ti, which reacted the chemical reaction and formed a transition layer in metallurgical combination. When the content of the Ti additive was 10%, the Brinell hardness (HB) of ZTA/HCCI composite was 573.1 N/mm(2) at room temperature, and the wear-resistant properties were more than 3.8 times of pure HCCI. After thermal treatment, the HB and wear resistance of 10% Ti-ZTA/HCCI composites increased significantly which could reach 629.8 N/mm(2) and were more than 4.3 times of the pure HCCI, respectively.
引用
收藏
页码：1289 / 1303
页数：15
相关论文
共 50 条
  • [41] Deposition mechanism of ceramic reinforced metal matrix composites via cold spraying
    Wang, Zhongyu
    Mao, Pengcheng
    Huang, Chunjie
    Yu, Pengfei
    Li, Wenya
    Yin, Shuo
    ADDITIVE MANUFACTURING, 2024, 85
  • [42] A Study of the Wear Mechanism of Composites Modified with Silicate Filler
    Danilova, Sakhayana N.
    Yarusova, Sofia B.
    Lazareva, Nadezhda N.
    Buravlev, Igor Yu.
    Shichalin, Oleg O.
    Papynov, Evgeniy K.
    Zhevtun, Ivan G.
    Gordienko, Pavel S.
    Okhlopkova, Aitalina A.
    CERAMICS-SWITZERLAND, 2022, 5 (04): : 731 - 747
  • [43] Effect of heat treatment on the wear behavior of zircon reinforced aluminium matrix composites
    Sharma, Sandeep
    Kumar, Suresh
    Nanda, Tarun
    Pandey, O. P.
    MATERIALS RESEARCH EXPRESS, 2019, 6 (05)
  • [44] Microstructures and Wear Behavior of the TiC Ceramic Particulate Locally Reinforced Steel Matrix Composites from a Cu-Ti-C System
    Liang, Yunhong
    Zhao, Qian
    Han, Zhiwu
    Zhang, Zhihui
    Li, Xiujuan
    Ren, Luquan
    ISIJ INTERNATIONAL, 2015, 55 (01) : 319 - 325
  • [45] Abrasive wear behavior of particle reinforced ultrahigh molecular weight polyethylene composites
    Liu, CZ
    Ren, LQ
    Arnell, RD
    Tong, J
    WEAR, 1999, 225 : 199 - 204
  • [46] A Review of the Friction and Wear Behavior of Particle-Reinforced Aluminum Matrix Composites
    Wang, Yunlei
    Zhang, Jie
    LUBRICANTS, 2023, 11 (08)
  • [47] Wear behavior of sansevieria cylindrica and E-glass reinforced polyester composites
    Sakthivel, Munisamy
    Srinivasan, Kandasamy
    Kumar, A. G. Ganesh
    MATERIALS TESTING, 2019, 61 (03) : 239 - 242
  • [48] Wear behavior of boron-carbide reinforced aluminum surface composites fabricated by Friction Stir Processing
    Mehta, K. M.
    Badheka, V. J.
    WEAR, 2019, 426 : 975 - 980
  • [49] Study on preparation and wear resistance of gradient transition ceramic coatings
    Yang Yueying
    Lin Fen
    Wang Jianjiang
    Liu Hongwei
    Fu Yongxin
    RARE METAL MATERIALS AND ENGINEERING, 2007, 36 : 512 - 515
  • [50] Study on the Interface Characteristics and Wear Resistance of Metal Matrix Composites at High Temperature
    Zhang Wen-Li
    Wu Cheng-Ling
    AGRO FOOD INDUSTRY HI-TECH, 2017, 28 (01): : 1209 - 1213
12345