Effect of binary raw materials replacement (quartz and feldspar) for porcelain chamotte on the electro-technical siliceous porcelain properties

被引：3

作者：

Rodriguez, Eden A. ^{[1
]}

Diaz-Tato, Leonel ^{[1
]}

Lopez-Perales, J. F. ^{[1
]}

Gonzalez-Carranza, Yadira ^{[1
]}

机构：

[1] Univ Autonoma Nuevo Leon UANL, Fac Ingn Mecan & Electr FIME, Programa Doctoral Ingn Mat, San Nicolas De Los Garza, Nuevo Leon, Mexico

来源：

FRONTIERS IN MATERIALS | 2023年 / 10卷

基金：

英国科研创新办公室;

关键词：

electro-technical porcelain; chamotte; microstructure; mechanical properties; sustainable material; replacement; MICROSTRUCTURAL EVOLUTION; MULLITE FORMATION; FIRED PORCELAIN; WASTE; INSULATORS; STRENGTH; FABRICATION; ALUMINA; SUBSTITUTION; BEHAVIOR;

D O I：

10.3389/fmats.2023.1322898

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The hurry for ecological practices and waste control has emerged as an obligation in modern times, demanding precise strategies to restrain waste accumulation and to stimulate recycling and reuse actions to lower the climate effect. The replacement of binary raw materials for porcelain chamotte waste in siliceous porcelain was studied to obtain eco-friendly high-voltage porcelain. Quartz and feldspar were progressively replaced by 5, 10, and 15 wt.% of porcelain chamotte in a conventional siliceous electro-technical porcelain composition. The replacement effect on sintered samples at 1250 degrees C under industrial heat treatment was evaluated by measuring the linear shrinkage, bulk density, porosity, flexural strength, and microhardness technological properties. Phase analysis was carried out by X-ray diffraction. Microstructural characteristics were studied using a scanning electron microscope. The results showed that chamotte-containing samples reached bulk densities of about 2.36 g/cm3 and a porosity percentage near zero. The maximum flexural strength value at glazed states was 87.8 MPa, for 15 wt.% scrap-containing samples. X-ray diffraction studies revealed a higher mullite phase content in chamotte-containing samples. Scanning electronic microscopy images of the polished and etched specimens show the presence of quartz grains and secondary mullite needles embedded in a feldspathic vitreous matrix. The properties reached by the chamotte-containing samples are attractive since the values obtained in terms of flexural strength, density, and porosity are compared to those reported for conventional siliceous porcelain were obtained. The most noticeable result was observed in flexural resistance. The glazed porcelain bodies showed a flexural strength improvement of about 15%. Then, these porcelain compositions suggest an alternative to produce a more sustainable, affordable, and environmentally-friendly porcelain insulator product.

引用

页数：15

共 82 条

[11] Improvement of mechanical and dielectric properties of porcelain insulators using economic raw materials [J].

Belhouchet, Khaled ;

Bayadi, Abdelhafid ;

Belhouchet, Hocine ;

Romero, Maximina .

BOLETIN DE LA SOCIEDAD ESPANOLA DE CERAMICA Y VIDRIO, 2019, 58 (01) :28-37

[12]

Benavidez E., 1999, 6 C EXH EUR CER SOC

[13]

Bragança S. R., 2004, Cerâmica, V50, P291

[14]

Brito J., 2013, Recycled aggregate in concrete. Green energy and technology, P23

[15]

Buchanan R.C., 1991, PROPERTIES CERAMIC I

[16] Non traditional raw material in ceramic industry [J].

Caligaris, R ;

Quaranta, N ;

Caligaris, M ;

Benavidez, E .

BOLETIN DE LA SOCIEDAD ESPANOLA DE CERAMICA Y VIDRIO, 2000, 39 (05) :623-626

[17]

Campos M.A., 2015, Investigacion y Desarrollo, V7, P30

[18] Valorisation of boron mining wastes in the production of wall and floor tiles [J].

Cicek, Bugra ;

Karadagli, Emirhan ;

Duman, Fatma .

CONSTRUCTION AND BUILDING MATERIALS, 2018, 179 :232-244

[19] Glassy wastes as feldspar substitutes in porcelain stoneware tiles: Thermal behaviour and effect on sintering process [J].

Conte, Sonia ;

Zanelli, Chiara ;

Molinari, Chiara ;

Guarini, Guia ;

Dondi, Michele .

MATERIALS CHEMISTRY AND PHYSICS, 2020, 256

[20] Predicting Viscosity and Surface Tension at High Temperature of Porcelain Stoneware Bodies: A Methodological Approach [J].

Conte, Sonia ;

Zanelli, Chiara ;

Ardit, Matteo ;

Cruciani, Giuseppe ;

Dondi, Michele .

MATERIALS, 2018, 11 (12)

← 1 2 3 4 5 6 7 8 9 →