Role of Re in NiAl bond coating on isothermal oxidation behavior of a thermal barrier coating system at 1100 °C

被引：12
作者：
Peng, X. [1 ,2 ]
Li, W. [1 ]
Fu, L. B. [1 ]
Li, Y. T. [1 ,2 ]
Jiang, S. M. [1 ]
Gong, J. [1 ]
Sun, C. [1 ]
机构：
[1] Chinese Acad Sci, Inst Met Res, Shi Changxu Innovat Ctr Adv Mat, Shenyang 110016, Peoples R China
[2] Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China
来源：
CORROSION SCIENCE | 2023年 / 218卷
关键词：
Thermal barrier coatings; Rhenium; Oxidation; Superalloys; Failure mode; SUPERALLOY; MECHANISMS; FAILURE; SCALES; OXIDE; TRANSFORMATION; SPALLATION; STABILITY; SUBSTRATE; PLATINUM;
D O I：
10.1016/j.corsci.2023.111151
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Role of Re in NiAl bond coating on intermittent isothermal oxidation behavior of thermal barrier coatings (TBCs) was researched in this study. Isothermal oxidation behaviors of NiAl-YSZ coatings with and without Re were investigated at 1100 & DEG;C. Results showed that NiAlRe-YSZ coating revealed lower level of & beta; to & gamma;& PRIME; phase transformation, and less severe delamination of YSZ was observed compared with NiAl-YSZ coating after 300 h oxidation. Moreover, the synergistic effect of Re and Zr/Y jointly improved delamination resistance of NiAlReYSZ coating during oxidation. Severe internal oxidation and rumpling prompted the delamination of YSZ for NiAl-YSZ coating without Re.
引用
收藏
页数：11
相关论文
共 52 条
  • [1] The microstructures of base/modified RR2072 SX superalloys and their effects on creep properties at elevated temperatures
    Chen, QZ
    Jones, N
    Knowles, DM
    [J]. ACTA MATERIALIA, 2002, 50 (05) : 1095 - 1112
  • [2] Thermal barrier coatings technology: critical review, progress update, remaining challenges and prospects
    Darolia, R.
    [J]. INTERNATIONAL MATERIALS REVIEWS, 2013, 58 (06) : 315 - 348
  • [3] Microstructure of Carbides at Grain Boundaries in Nickel Based Superalloys
    Dong, Xiaoming
    Zhang, Xiaoli
    Du, Kui
    Zhou, Yizhou
    Jin, Tao
    Ye, Hengqiang
    [J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2012, 28 (11) : 1031 - 1038
  • [4] Rhenium oxidation by steam at high temperatures
    Duriez, C
    [J]. OXIDATION OF METALS, 2004, 61 (1-2): : 49 - 67
  • [5] Mechanisms controlling the durability of thermal barrier coatings
    Evans, AG
    Mumm, DR
    Hutchinson, JW
    Meier, GH
    Pettit, FS
    [J]. PROGRESS IN MATERIALS SCIENCE, 2001, 46 (05) : 505 - 553
  • [6] ON THE MECHANICS OF DELAMINATION AND SPALLING IN COMPRESSED FILMS
    EVANS, AG
    HUTCHINSON, JW
    [J]. INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 1984, 20 (05) : 455 - 466
  • [7] Assessment of thermodynamic parameters in the system ZrO2-Y2O3-Al2O3
    Fabrichnaya, O
    Aldinger, F
    [J]. ZEITSCHRIFT FUR METALLKUNDE, 2004, 95 (01): : 27 - 39
  • [8] Progress in coatings for gas turbine airfoils
    Goward, GW
    [J]. SURFACE & COATINGS TECHNOLOGY, 1998, 108 (1-3) : 73 - 79
  • [9] Effect of Mo, Ta, and Re on high-temperature oxidation behavior of minor HI doped β-NiAl alloy
    Han, Baohong
    Ma, Yue
    Peng, Hui
    Zheng, Lei
    Guo, Hongbo
    [J]. CORROSION SCIENCE, 2016, 102 : 222 - 232
  • [10] Influence of sulfur, platinum, and hafnium on the oxidation behavior of CVD NiAl bond coatings
    Haynes, JA
    Pint, BA
    More, KL
    Zhang, Y
    Wright, IG
    [J]. OXIDATION OF METALS, 2002, 58 (5-6): : 513 - 544
123456