Synthesis of Nanocrystalline Yttrium Oxide and Evolution of Morphology and Microstructure during Thermal Decomposition of Y2(C2O4)3Greek ano teleia10H2O

A study of the morphology and evolution of the microstructure during thermal decomposition of Y-2(C2O4)(3)Greek ano teleia10H(2)O was conducted, and the stages and factors having the greatest impact on particle size and specific surface area were identified. The effect of the yttrium oxalate hexahydrate phases on the course of decomposition was also investigated. The evolution of the morphology and microstructure of decomposition products was explained from the analysis of volume shrinkage at various stages of the reaction. The formation of oxycarbonate is accompanied by the largest shrinkage during the reaction. At this stage, there is a significant increase in the specific surface area to 60-90 m(2)/g. Conversely, the morphology and microstructure of the particles during the transformation of oxycarbonate into yttrium oxide change insignificantly. Yttrium oxide powders obtained from the monoclinic and triclinic hexahydrate phases have the same specific surface area, but different morphology and bulk density due to pseudomorph formation. The carbon formed during thermolysis was shown to affect the specific surface area of the decomposition product. Two methods for producing yttrium oxide with high specific surface area have been proposed, and nanocrystalline yttrium oxide with a specific surface area of 65 m(2)/g was obtained.