Effect of Post-Weld Heat Treatment on Microstructure and Hardness of Laser Beam Welded 17-4 PH Stainless Steel

This article presents the results of research on the development of the technology of laser beam butt welding of 17-4 PH stainless steel sheets and the technology of post-weld heat treatment (PWHT). The developed technology allows for favorable conditions to be obtained and for the appropriate microstructure and hardness to exist in the weld area. Moreover, it enables the fulfillment of a number of specific requirements beyond the possibilities of manual welding and other methods. The tests performed include the analysis of the microstructure with the use of light microscopy (LM) for the materials after welding and PWHT. The applied PWHT showed changes in the microstructure and mechanical properties. In all weld areas the martensitic microstructure was observed. The homogeneity of the microstructure in the area of the welded joint after PWTH was revealed. In the as-welded condition and after the PWHT with aging at 481 degrees C, the hardness was 440 HV5, but after aging at 621 degrees C, it decreased to 330-340 HV5.