Study on corrosion behavior of Ni-P/Ni-Cu-P superhydrophobic composite coatings preparation on L360 steel by two-step method

被引:26
作者
Zhang, Weizhi [1 ,2 ,3 ]
Liao, Dandan [4 ]
Tang, Dezhi [5 ]
Han, Enhou [1 ,2 ]
Wang, Jun [4 ]
机构
[1] Univ Sci & Technol China, Sch Mat Sci & Engn, 96 Jinzhai Rd, Hefei 230026, Anhui, Peoples R China
[2] Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China
[3] PetroChina, Oil Gas & New Energies Co, Beijing 100007, Peoples R China
[4] Sichuan Univ, Sch Mech Engn, Chengdu 610065, Peoples R China
[5] PetroChina Planning & Engn Inst, Beijing 100083, Peoples R China
来源
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T | 2023年 / 23卷
关键词
Composite coating; Electroless plating; Superhydrophobicity; Electrochemical corrosion; Erosion corrosion; MICROSTRUCTURE EVOLUTION; RESISTANCE; SUSPENSION; SURFACE; ENHANCEMENT; FABRICATION; NICKEL; ALLOYS;
D O I
10.1016/j.jmrt.2023.01.224
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The two-step process of electroless plating and electrodeposition was used to successfully prepare a bilayer composite film by electroplating a Ni-Cu-P film with hydrophobic properties on the Ni-P film. The histological features of the two membrane layers were compared. The L360 pipeline steel, Ni-P coating and Ni-Cu-P composite film were eval-uated by electrochemical test and erosion corrosion method. Under simulated seawater conditions, the material properties changed before and after different periods of service. The experimental results show that the introduction of Cu can inhibit the growth of cellular structures on the surface of the coating, increase the number of nucleation points, and improve the microstructure of the coating during the deposition of Ni-Cu-P films. The Ni-P/Ni-Cu-P bilayer composite film has a pinecone-like convex structure, which can greatly reduce the surface energy of the film layer and endow the film layer with hydro-phobicity. At the same time, it effectively resists the adsorption of water and other external impurities on its surface, and has good anti-fouling performance, thereby slowing down the surface corrosion and improving corrosion resistance. In addition, copper enables the composite coating to have passivation and a uniform and dense coating structure, which is the main reason for the improvement of the corrosion protection performance of the composite coating. The protective effect of the coating can effectively improve the elec-trochemical resistance and erosion resistance of L360. The Ni-P/Ni-Cu-P bilayer com-posite film reduces the electrochemical corrosion rate of the substrate from 0.417mmpY to 0.025mmpY, and the scouring weight loss rate of the film decreases to 0.05% of the substrate. (c) 2023 The Authors. Published by Elsevier B.V. This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/).
引用
收藏
页码:3035 / 3047
页数:13
相关论文
共 43 条
[41]   Superhydrophobic surface constructed on electrodeposited silica films by two-step method for corrosion protection of mild steel [J].
Zhang, Xue-Fen ;
Chen, Rui-Jiao ;
Hu, Ji-Ming .
CORROSION SCIENCE, 2016, 104 :336-343
[42]   Electroless Ni-Cu-P-PTFE composite coatings and their anticorrosion properties [J].
Zhao, Q ;
Liu, Y .
SURFACE & COATINGS TECHNOLOGY, 2005, 200 (07) :2510-2514
[43]   Dependence of the abnormal protective property on the corrosion product film formed on H2S-adjacent API-X52 pipeline steel [J].
Zheng, Shuqi ;
Zhou, Chengshuang ;
Chen, Xingyang ;
Zhang, Lin ;
Zheng, Jinyang ;
Zhao, Yongzhi .
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2014, 39 (25) :13919-13925