Ultimate tensile capacity of hot-dip galvanized ultra-high-strength steel cut edges and welded joints

被引：1
|
作者：
Lipiainen, Kalle [1 ]
Ahola, Antti [1 ]
Javaheri, Vahid [2 ]
Bjork, Timo [1 ]
机构：
[1] Lappeenranta Lahti Univ Technol LUT, Lab Steel Struct, POB 20, Lappeenranta 53851, Finland
[2] Univ Oulu, Ctr Adv Steels Res, Mat & Mech Engn, Oulu, Finland
来源：
WELDING IN THE WORLD | 2023年 / 67卷 / 12期
关键词：
Tensile strength; Hot-dip galvanizing; Ultra-high-strength steel; Cut edge; Welded joint;
D O I：
10.1007/s40194-023-01611-6
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Tensile tests of 6-mm-thick hot-dip galvanized (HDG) S960 specimens were performed. The study focused on room temperature but also - 40 degrees C cold temperature tests were performed to ensure material behavior and reliability. Microstructural characterization using a scanning electron microscopy was performed to evaluate the influence of HDG. The results showed that HDG slightly decreased the tensile strength of plain S960 specimens whereas its effect on welded joints was not significant in both room and cold temperatures.
引用
收藏
页码：2779 / 2789
页数：11
相关论文
共 50 条
  • [41] Global-local fatigue approaches for snug-tight and preloaded hot-dip galvanized steel bolted joints
    Souto, Carlos D. S.
    Gomes, Vitor M. G.
    Da Silva, Lucas F. R. C.
    V. Figueiredo, Miguel
    Correia, Jose A. F. O.
    Lesiuk, Grzegorz
    Fernandes, Antonio A.
    De Jesus, Abilio M. P.
    INTERNATIONAL JOURNAL OF FATIGUE, 2021, 153
  • [42] Effect of the Interface Microstructure of Hot-Dip Galvanizing High-Strength Automobile Steel on Its Tensile Fracture Behaviors
    Yu Jiaying
    Wang Hua
    Zheng Weisen
    He Yanlin
    Wu Yurui
    Li Lin
    ACTA METALLURGICA SINICA, 2020, 56 (06) : 863 - 873
  • [43] Characterization of Intermetallic Phases on Hot-dip Galvanized High-strength Steels by Means of Bromine Etching
    Maderthaner, Magdalena
    Jarosik, Alexander
    Haubner, Roland
    BHM Berg- und Huttenmannische Monatshefte, 2019, 164 (05): : 196 - 199
  • [44] Effect of eps treatment on surface quality of hot dip galvanized high strength steel
    Ma, Er-Qing
    Cui, Lei
    Peng, Meng-Du
    Xiao, Yang-Yang
    Liu, Yang
    Wang, Zhong-Le
    Surface Technology, 2020, 49 (06): : 352 - 358
  • [45] HOT DIP GALVANIZED HIGH-STRENGTH STEEL FOR DRAWING OF AUTOMOBILE STRUCTURAL PARTS
    BRUN, C
    PATOU, P
    SCHOENENBERGER, A
    REVUE DE METALLURGIE-CAHIERS D INFORMATIONS TECHNIQUES, 1984, 81 (06): : 507 - 519
  • [46] The Low-cycle Fatigue Strength of Laser-welded Ultra-high-strength Steel
    Keskitalo, Markku
    Mantyjarvi, Kari
    Kiuru, Toni
    SHEET METAL 2011, 2011, 473 : 281 - 289
  • [47] HOT DIP GALVANIZED HIGH-STRENGTH STEEL FOR DRAWING OF AUTOMOBILE STRUCTURAL PARTS
    BRUN, C
    PATOU, P
    SCHOENENBERGER, A
    REVUE DE METALLURGIE-CAHIERS D INFORMATIONS TECHNIQUES, 1983, 80 (11): : E162 - E162
  • [48] Joining of Hot-Dip Coated High-Strength Steel Sheets by Mechanical Clinching
    Abe, Yohei
    Kato, Toru
    Kishimoto, Masaya
    Mori, Ken-ichiro
    STEEL RESEARCH INTERNATIONAL, 2010, 81 (09) : 1128 - 1131
  • [49] SPRINGBACK OF HOT STAMPING AND DIE QUENCHING WITH ULTRA-HIGH-STRENGTH BORON STEEL
    Bao, J.
    Liu, H.
    Xing, Z.
    Song, B.
    Yang, Y.
    ENGINEERING REVIEW, 2013, 33 (03) : 151 - 156
  • [50] TESTING OF BOND STRENGTH HOT-DIP GALVANIZED STEEL REINFORCEMENT CONCRETE WITH VERIFICATION CAUSES CHANGES AT THE INTERFACE TRANSITION ZONE
    Pokorny, Petr
    Kouril, Milan
    Novak, Pavel
    21ST INTERNATIONAL CONFERENCE ON METALLURGY AND MATERIALS (METAL 2012), 2012, : 1058 - 1064
12345