Effects of Ce content on the modification of Mg 2 Si phase in Mg-5Al-2Si alloy

The effect of Ce content (0-1.6 wt.%) on the modification of Mg 2 Si phase in the as-cast Mg-5Al-2Si alloy was investigated. The original Chinese script type Mg 2 Si phase was refined distinctly and transformed to dispersive block shape gradually by adding Ce element. The length of Chinese script type Mg 2 Si phase was reduced from 110 to 50 & mu;m with increasing Ce content to 1.6 wt.%. The results calculated by Pandat software indicated that the added Ce element first combined with Si to form CeSi 2 phase, which could serve as the heterogeneous nucleation of Mg 2 Si phase due to the small lattice mismatch of 7.97%. The modification of Mg 2 Si phase was mainly attributed to the facts that Ce changed the growth steps of Mg 2 Si phase and CeSi 2 promoted the nucleation of Mg 2 Si phase. With increasing Ce content from 0 wt.% to 1.6 wt.%, the YS, UTS and EL at 150 & DEG;C were improved from 67.7 MPa, 91.2 MPa and 1.6% to 84.2 MPa, 128 MPa and 7.5%, respectively. & COPY; 2021 Chongqing University. Publishing services provided by Elsevier B.V. on behalf of KeAi Communications Co. Ltd. This is an open access article under the CC BY-NC-ND license ( http://creativecommons.org/licenses/by-nc-nd/4.0/ ) Peer review under responsibility of Chongqing University