The Effect of Superplasticizers on Eco-friendly Low-Energy One-Part Alkali-Activated Slag

One-part alkali-activated materials (OP-AAM) have become a promising binder with low carbon and energy requirements associated with superior mechanical and durability characteristics. This study aims to employ commercial superplasticizers (naphthalene-based "Nb-SP" and polycarboxylate-based "PCb-SP"), as well as laboratory-prepared one (phenol-formaldehyde sulfanilate "PFS-SP") in enhancing the properties of OP-AAM. The main problem of superplasticizers (SPs) in the AAM is their hydrolysis in the alkaline activator (NaOH) used in the activation reactions. Therefore, the thermo-chemical treatment process was utilized to mitigate the high activator alkalinity by impeding the NaOH in the aluminosilicate precursor matrix. The OP-AAM was fabricated from thermo-chemical treatment powder (TCT-P) resulting from sintering blast furnace slag (GGBFS) with 10 wt% NaOH at 300 and 500 & DEG;C. The XRD-pattern showed that NaOH was impeded in the GGBFS via sodium aluminum silicate phase formation after sintering at 500 & DEG;C. The results showed that the admixed OP-AAM prepared from TCT-P at 500 & DEG;C greatly enhanced the workability and mechanical properties. The PFS-SP proved its efficiency in improving the properties of OP-AAM prepared TCT-P at 300 and 500 & DEG;C, referring to its high stability in an alkaline medium. While PCb-SP reinforced the properties of OP-AAM prepared from TCT-P at 500 & DEG;C only, proving that PCb-SP promotes high capability in TCT-P-500 as well as in Portland cement.