Study on the oxidation resistance mechanism of self-healable NiAl coating deposited by atmospheric plasma spraying

被引:7
作者
Zhang, Li [1 ]
Wang, Di [1 ]
Liao, Xian-Jin [1 ]
Chen, Rui [1 ]
Luo, Xiao-Tao [1 ]
Li, Chang-Jiu [1 ]
机构
[1] Xi An Jiao Tong Univ, Sch Mat Sci & Engn, State Key Lab Mech Behav Mat, Xian 710049, Shaanxi, Peoples R China
关键词
HIGH-TEMPERATURE OXIDATION; MCRALY BOND COATS; CYCLIC OXIDATION; BEHAVIOR; CORROSION; FAILURE; LIFETIME; HVOF;
D O I
10.1038/s41529-023-00383-0
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
A dense NiAl coating with low oxide content was deposited on the GH4202 superalloy substrate by atmospheric plasma spraying (APS) using carbon-containing Ni/Al composite powders. Compared with traditional APS NiAl coatings with high oxide content, this coating exhibits better long-term oxidation resistance at 900 & DEG;C in air. For the NiAl coating with low oxide content, it was found that the improved inter-splat bonding, due to limited oxide inclusions, promotes the formation of a continuous protective Al2O3 layer on the coating surface during oxidation. During long-term oxidation, the dispersion of oxide scales within the coating and element diffusion across splats result in the in-situ healing of unbonded inter-splat interfaces.
引用
收藏
页数:11
相关论文
共 47 条
[41]   Ablation resistance under different heat fluxes of HfC-ZrC-SiC multiphase coating prepared by supersonic atmospheric plasma spraying for C/C composites [J].
Yang Yang ;
Chun Zhao ;
Qiaojuan Gong ;
Jie Wang .
Journal of the Korean Ceramic Society, 2020, 57 :152-160
[42]   High-Temperature Oxidation Resistance Mechanism and Thermal Shock Performance of CoCrTaAlY/YSZ Thermal Barrier Coatings Fabricated Using Plasma Spraying and Laser Cladding [J].
Gu Z. ;
Lei J. ;
Dou J. ;
Guo J. .
Zhongguo Jiguang/Chinese Journal of Lasers, 2019, 46 (08)
[43]   The growth mechanism and corrosion resistance of laser-assisted plasma electrolytic oxidation (PEO) composite coating on AZ31B magnesium alloy [J].
Wu, Guolong ;
Li, Lin ;
Chen, Xianghui ;
Zhu, Lebin ;
Wang, Ye ;
Wen, Chen ;
Yao, Jianhua .
JOURNAL OF MAGNESIUM AND ALLOYS, 2025, 13 (02) :760-776
[44]   Formation Mechanism of a Y-modified Cr-Al Coating Co-deposited on DZ125 Alloy and Its High-temperature Oxidation Resistance [J].
Li Yongquan ;
Liang Guodong ;
Tian Xingda ;
Wang Cunxi ;
He Ninghui ;
Qin Chun .
JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2022, 37 (02) :270-276
[45]   Study on the Wear Resistance of 6061 Aluminum Alloy Bipolar Plasma Electrolytic Oxidation Ceramic Coating by the Addition of K2ZrF6 [J].
Tong, Rui ;
Zhou, Shiquan ;
Li, Hongtao ;
Tao, Xiang ;
Chen, Jian .
MATERIALS, 2025, 18 (13)
[46]   High-Temperature Thermal Protective Performance of High-Entropy Rare-Earth Tantalate (Nd0.2Dy0.2Ho0.2Y0.2Er0.2)TaO4 Coating Deposited By Atmospheric Plasma Spraying [J].
Zhang, Yulong ;
Zhu, Jinpeng ;
Zheng, Jiayi ;
Wang, Kai ;
Li, Yujing ;
Yang, Kaijun ;
Li, Mingliang ;
Wang, Hailong ;
He, Jilin .
JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2025,
[47]   A study into enhanced oxidation resistance and its mechanism in Cr1-xAlxN/CrN/Cr multilayer films deposited on 9-12 % Cr heat-resistant steel [J].
Yang, Wen-Sheng ;
Chen, Sheng-Chi ;
Pei, Yu-Bing ;
Chen, Rong-Zhi ;
Guo, Han-Jie .
CERAMICS INTERNATIONAL, 2021, 47 (13) :19134-19141