Structure Evolution and Mechanical Properties of Sheet Al-2Cu-1.5Mn-1Mg-1Zn (wt.%) Alloy Designed for Al20Cu2Mn3 Disperoids

This work was focused on studying the possibility of increasing the strength of non-heat-treatable sheet alloy Al2Cu1.5Mn (wt.%) by the joint addition of 1% Mg and 1% Zn. The effect of these elements on the structure and mechanical properties of the new sheet Al2Cu1.5Mn alloy designed for Al20Cu2Mn3 dispersoids has been studied by calculations and experimental methods. The obtained data on the phase composition, microstructure, and physical and mechanical properties of the new alloy for different processing routes (including hot rolling, cold rolling, and annealing) have been compared with those for the ternary Mg- and Zn-free alloy. It has been shown that the formation of nanosized Al20Cu2Mn3 dispersoids (similar to 7 vol.%) provides for the preservation of the non-recrystallized grain structure after annealing at up to 400 degrees C (3 h), while Mg and Zn have a positive effect on the strength due to the formation of alloyed aluminum solid solution. As a result, cold-rolled sheets of the Al2Cu1.5Mn1Mg1Zn model alloy showed a substantially higher strength performance after annealing at 400 degrees C in comparison with the ternary reference alloy. In particular, the UTS is similar to 360 vs. similar to 300 MPa, and the YS is 280 vs. 230 MPa. For the example of the Al2Cu1.5Mn1Mg1Zn model alloy, it has been shown that the system is promising for designing new heat-resistant alloys as a sustainable alternative to the 2xxx alloys. The new alloy has an advantage over the commercial alloys (particularly, 2219, 2024, 2014), not only in manufacturability but also in thermal stability. The sheet production cycle for the model alloy is much shorter because the stages of homogenization, solution treatment, and water quenching are excluded.