Dissolution behavior of spent MgO-C refractory in the CaO-SiO2-FeO slag system as a steelmaking flux

被引:11
作者
Zhu, Liang [1 ]
Liu, Chun-yang [1 ,2 ]
Du, Chuan-ming [3 ]
Huang, Fu-xiang [1 ]
Sun, Yong-lin [1 ]
Jia, Yi [1 ]
Wang, Yan-feng [1 ]
Ma, Bei-yue [2 ]
机构
[1] Steelmaking Plant Beijing Shougang Co Ltd, Tangshan 064400, Peoples R China
[2] Northeastern Univ, Sch Met, Shenyang 110819, Peoples R China
[3] 3-11 Wenhua Rd, Shenyang, Peoples R China
基金
中国博士后科学基金;
关键词
MgO-C refractory; Steelmaking slag; Flux; Dissolution; CORROSION; DOLOMITE; MECHANISM; BRICKS; FINES;
D O I
10.1016/j.ceramint.2023.05.022
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
A large amount of spent MgO-C refractory is generated in steel plant every year. Because of the similarities in chemical and mineralogical composition of slag formers and MgO-C refractory, it is possible to reuse the spent MgO-C refractory as a steelmaking flux. To achieve this goal, it should promote the dissolution of MgO-C re-fractory during slag forming. In this study, the effect of slag composition on the dissolution behavior of spent MgO-C refractory in the CaO-SiO2-FeO slag system and the dissolution kinetics were investigated. It showed that the dissolution rate of MgO-C refractory was controlled by surface chemical reaction. The dissolution of MgO-C refractory led to an increase in the MgO content in slag while the FeO content decreased because the graphite in refractory was oxidized by FeO. Increasing temperature significantly promoted the dissolution of MgO-C refractory. The MgO-C refractory was readily dissolved in the low-basicity slag. A higher FeO content in slag was beneficial for the oxidation of graphite in refractory, resulting in better dissolution. The dissolution thickness of MgO-C refractory could exceed 4.0 mm under these conditions and its dissolution supplied some MgO to slag.
引用
收藏
页码:24931 / 24940
页数:10
相关论文
共 36 条
[1]   Phase formation in MgO-C refractories with different antioxidants [J].
Atzenhofer, C. ;
Harmuth, H. .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2021, 41 (14) :7330-7338
[2]   Recycling practices of crushed MgO-C bricks and dolomite sinter fines used as a slag conditioning additive in the EAF [J].
Avelar, T. C. ;
Veiga, A. F. ;
Gueguen, E. ;
Oliveira, J. R. .
WASTE MANAGEMENT AND THE ENVIRONMENT VI, 2012, 163 :259-270
[3]   Activity of iron oxide in steelmaking slag [J].
Basu, Somnath ;
Lahiri, Ashok Kumar ;
Seetharaman, Seshadri .
METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2008, 39 (03) :447-456
[4]   Microstructural characteristics and fracture mechanism of in situ pressureless-sintered MgAlON-MgO ceramic from spent MgO-C brick [J].
Cheng, Xiang ;
Miao, Xiwang ;
Liu, Lei ;
Zhang, Ying ;
Guo, Min ;
Cheng, Fangqin ;
Zhang, Mei .
MATERIALS CHARACTERIZATION, 2021, 179
[5]   Microstructure and properties of MgO-C refractory with different carbon contents [J].
Cheng, Yong ;
Zhu, Tianbin ;
Li, Yawei ;
Sang, Shaobai .
CERAMICS INTERNATIONAL, 2021, 47 (02) :2538-2546
[6]   Recycling MgO-C refractory in electric arc furnaces [J].
Conejo, A. N. ;
Lule, R. G. ;
Lopez, F. ;
Rodriguez, R. .
RESOURCES CONSERVATION AND RECYCLING, 2006, 49 (01) :14-31
[7]   Oxidation mechanism of MgO-C in air at various temperatures [J].
Ghosh, NK ;
Ghosh, DN ;
Jagannathan, KP .
BRITISH CERAMIC TRANSACTIONS, 2000, 99 (03) :124-128
[8]   Degradation of MgO-C refractories corroded by SiO2-Fe2O3-V2O5-TiO2-MnO-MgO slag [J].
Han, Bingqiang ;
Ke, Changming ;
Wei, Yaowu ;
Yan, Wen ;
Wang, Changmin ;
Chen, Fangyu ;
Li, Nan .
CERAMICS INTERNATIONAL, 2015, 41 (09) :10966-10973
[9]  
Hanagiri S., 2008, Nippon Steel Technical Report, V98, P93
[10]  
Hashemi B, 2006, J MATER SCI TECHNOL, V22, P826