Effect of Nano-Cr2O3 Dispersed W-Zr Alloys by Mechanical Alloying and Pressureless Conventional Sintering

被引:1
作者
Das, Bappa [1 ]
Khan, Atiqur Rahman [1 ]
Patra, Anshuman [1 ]
机构
[1] Natl Inst Technol, Dept Met & Mat Engn, Rourkela, India
关键词
fractography; mechanical alloying; sintering; strength; W-Zr alloy; wear; GRAIN-SIZE; DEFORMATION-BEHAVIOR; REFRACTORY-METALS; TUNGSTEN; MICROSTRUCTURE; FABRICATION; NI; DENSIFICATION; TEMPERATURE; NANOPOWDERS;
D O I
10.1007/s11665-023-08357-8
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Mechanical alloying is a preferred approach for producing tungsten (W)-zirconium (Zr)-based alloys due to their vast difference in melting point and insufficient synergic solubility. This study comprises fabrication of nano-chromium oxide (Cr2O3)-dispersed W-Zr alloys through mechanically alloying for 20 h followed by conventional sintering in inert (argon) atmosphere at 1400 and 1500 degrees C with a 2-h holding time. Alloys A, B, and C are designated as per the following compositions: 98.5W-0.5Zr-1(Cr2O3), 97.5W-0.5Zr-2(Cr2O3), and 98W-1Zr-1(Cr2O3), respectively. The effects of the Zr and Cr2O3 addition to W and sintering temperature have been discussed in relation to mechanical characteristics. The phase evaluation and microstructural behavior of the powders and sintered samples has been studied using x-ray diffraction, scanning electron microscopy (SEM), and transmission electron microscopy, respectively. The powder characterization after 20 h of milling through SEM has depicted a homogeneous mixture of Zr and Cr2O3 with W. Combined addition of Zr and Cr2O3 has resulted in a bimodal grain size distribution. The enhanced grain refinement coarse/fine particle count ratio due to mechanical alloying was observed in alloy A after 20 h, which was 1.57 compared to 2.6 in alloy C. The alloy A sintered at 1500 degrees C exhibited the highest densification (91%), hardness (13 GPa), wear resistance, and compression strength (1.37 GPa) due to better fraction of fine grains, solid solution, and dispersion strengthening compared to other alloys in both sintering temperatures.
引用
收藏
页码:5236 / 5256
页数:21
相关论文
共 62 条
[1]   Mechanical Behavior of W-Y2O3 and W-Ti Alloys from 25 A°C to 1000 A°C [J].
Aguirre, M. V. ;
Martin, A. ;
Pastor, J. Y. ;
Llorca, J. ;
Monge, M. A. ;
Pareja, R. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2009, 40A (10) :2283-2290
[2]   CONTACT AND RUBBING OF FLAT SURFACES [J].
ARCHARD, JF .
JOURNAL OF APPLIED PHYSICS, 1953, 24 (08) :981-988
[3]   EXCITATION FUNCTIONS OF (N,P) AND (N,2N) REACTIONS FOR SOME ISOTOPES OF K,MN,ZN AND CU [J].
BORMANN, M ;
LAMMERS, B .
NUCLEAR PHYSICS A, 1969, A130 (01) :195-&
[4]   Densification of nanocrystalline Y2O3 ceramic powder by spark plasma sintering [J].
Chaim, Rachman ;
Shlayer, Amit ;
Estournes, Claude .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2009, 29 (01) :91-98
[5]   The effects of alloying and milling on the formation of intermetallics in ODS tungsten heavy alloys [J].
Chen, Chun-Liang ;
Huang, Chun-Lin .
INTERMETALLICS, 2013, 41 :10-15
[6]   Effects of Heat Treatment on the Mechanical Properties of Fe-Based ER70S-6 Cladding on Aluminum Substrate Using Cold Metal Transfer Process [J].
Das, Bappa ;
Panda, Biranchi N. ;
Dixit, Uday S. .
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2024, 33 (01) :173-193
[7]   Fabrication of nano-La2O3 dispersed W-Zr alloy by mechanical alloying and conventional sintering [J].
Das, Bappa ;
Patra, Anshuman .
MATERIALS TODAY-PROCEEDINGS, 2022, 62 :6055-6060
[8]   Fabrication and characterization of nano-Cr2O3 dispersed mechanically alloyed and conventional sintered W-Zr alloys [J].
Das, Bappa ;
Patra, A. .
MATERIALS TODAY-PROCEEDINGS, 2020, 33 :5109-5115
[9]   Fabrication of W-Ti-Mo alloys and its microstructure, mechanical properties prepared by mechanical alloying [J].
Das, Bappa ;
Patra, A. .
MATERIALS TODAY-PROCEEDINGS, 2020, 26 :2845-2852
[10]   INFLUENCE OF MICROSTRUCTURE ON FRACTURE OF DRAWN TUNGSTEN WIRE [J].
FUNKENBUSCH, AW ;
BACON, F ;
LEE, D .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1979, 10 (08) :1085-1091