Effect of grain refinement induced by wire and arc additive manufacture (WAAM) on the corrosion behaviors of AZ31 magnesium alloy in NaCl solution

Additive manufacturing (AM) of Mg alloys has become a promising strategy for producing complex structures, but the corrosion perfor-mance of AM Mg components remains unexploited. In this study, wire and arc additive manufacturing (WAAM) was employed to produce single AZ31 layer. The results revealed that the WAAM AZ31 was characterized by significant grain refinement with non-textured crystal-lographic orientation, similar phase composition and stabilized corrosion performance comparing to the cast AZ31. These varied corrosion behaviors were principally ascribed to the size of grain, where cast AZ31 and WAAM AZ31 were featured by micro galvanic corrosion and intergranular corrosion, respectively.(c) 2022 Chongqing University. Publishing services provided by Elsevier B.V. on behalf of KeAi Communications Co. Ltd. This is an open access article under the CC BY-NC-ND license ( http://creativecommons.org/licenses/by-nc-nd/4.0/ ) Peer review under responsibility of Chongqing University