Synthesis of Ti3SiC2 Phases and Consolidation of MAX/SiC Composites-Microstructure and Mechanical Properties

被引：6
作者：
Wozniak, Jaroslaw [1 ]
Petrus, Mateusz [1 ]
Cygan, Tomasz [1 ]
Adamczyk-Cieslak, Boguslawa [1 ]
Moszczynska, Dorota [1 ]
Olszyna, Andrzej Roman [1 ]
机构：
[1] Warsaw Univ Technol, Fac Mat Sci & Engn, PL-02507 Warsaw, Poland
来源：
MATERIALS | 2023年 / 16卷 / 03期
关键词：
sintering; composites; mechanical properties; SiC; MAX phases; REACTIVE SYNTHESIS; CRACK-PROPAGATION; OXIDATION; POWDERS; BULK; SI; TI;
D O I：
10.3390/ma16030889
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
The article describes the Ti3SiC2 powder synthesis process. The influence of the molar ratio and two forms of carbon on the phase composition of the obtained powders was investigated. The synthesis was carried out using a spark plasma sintering (SPS) furnace. In addition, using the obtained powders, composites reinforced with SiC particles were produced. The obtained results showed no effect of the carbon form and a significant impact of annealing on the purity of the powders after synthesis. The composites were also consolidated using an SPS furnace at two temperatures of 1300 and 1400 degrees C. The tests showed low density and hardness for sinters from 1300 degrees C (maximum 3.97 g/cm(3) and 447 HV5, respectively, for composite reinforced with 10% SiC). These parameters significantly increase for composites sintered at 1400 degrees C (maximum density 4.43 g/cm(3) and hardness 1153 HV5, for Ti3AlC2-10% SiC). In addition, the crack propagation analysis showed mechanisms typical for granular materials and laminates.
引用
收藏
页数：13
相关论文
共 30 条
  • [1] Barsoum M W, 2006, PHYS PROPERTIES MAX
  • [2] Long time oxidation study of Ti3SiC2,Ti3SiC2/SiC, and Ti3SiC2/TiC composites in air
    Barsoum, MW
    Ho-Duc, LH
    Radovic, M
    El-Raghy, T
    [J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2003, 150 (04) : B166 - B175
  • [3] The MN+1AXN phases:: A new class of solids;: Thermodynamically stable nanolaminates
    Barsoum, MW
    [J]. PROGRESS IN SOLID STATE CHEMISTRY, 2000, 28 (1-4) : 201 - 281
  • [4] Layered machinable ceramics for high temperature applications
    Barsoum, MW
    Brodkin, D
    ElRaghy, T
    [J]. SCRIPTA MATERIALIA, 1997, 36 (05) : 535 - 541
  • [5] A Mode I cohesive law characterization procedure for through-the-thickness crack propagation in composite laminates
    Bergan, Andrew
    Davila, Carlos
    Leone, Frank
    Awerbuch, Jonathan
    Tan, Tein-Min
    [J]. COMPOSITES PART B-ENGINEERING, 2016, 94 : 338 - 349
  • [6] Synthesis of Ti3SiC2 powders:: Reaction mechanism
    Cordoba, Jose M.
    Sayagues, Maria J.
    Alcala, Maria D.
    Gotor, Francisco J.
    [J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2007, 90 (03) : 825 - 830
  • [7] Microstructure and Mechanical Properties of Alumina Composites with Addition of Structurally Modified 2D Ti3C2 (MXene) Phase
    Cygan, Tomasz
    Wozniak, Jaroslaw
    Petrus, Mateusz
    Lachowski, Artur
    Pawlak, Wojciech
    Adamczyk-Cieslak, Boguslawa
    Jastrzebska, Agnieszka
    Rozmyslowska-Wojciechowska, Anita
    Wojciechowski, Tomasz
    Ziemkowska, Wanda
    Olszyna, Andrzej
    [J]. MATERIALS, 2021, 14 (04) : 1 - 18
  • [8] Short SiC fiber/Ti3SiC2MAX phase composites: Fabrication and creep evaluation
    Dash, Apurv
    Malzbender, Juergen
    Vassen, Robert
    Guillon, Olivier
    Gonzalez-Julian, Jesus
    [J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2020, 103 (12) : 7072 - 7081
  • [9] Optimization of the Ti3SiC2 MAX phase synthesis
    El Saeed, M. A.
    Deorsola, F. A.
    Rashad, R. M.
    [J]. INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2012, 35 : 127 - 131
  • [10] Ti2AlC coatings deposited by High Velocity Oxy-Fuel spraying
    Frodelius, Jenny
    Sonestedt, Marie
    Bjorklund, Stefan
    Palmquist, Jens-Petter
    Stiller, Krystyna
    Hogberg, Hans
    Hultman, Lars
    [J]. SURFACE & COATINGS TECHNOLOGY, 2008, 202 (24) : 5976 - 5981
123