Modified pine needles as a formaldehyde scavenger for urea-formaldehyde resin in plywood production

被引:12
作者
Dukarska, Dorota [1 ]
Kawalerczyk, Jakub [1 ]
Kmieciak, Jakub [1 ]
机构
[1] Poznan Univ Life Sci, Fac Forestry & Wood Technol, Dept Mech Wood Technol, Poznan, Poland
关键词
WEAR PROPERTIES; WOOD ADHESIVES; SOY FLOUR; FILLER; PERFORMANCE; WASTE; WATER; ACID; BARK; COMPOSITES;
D O I
10.1007/s00107-023-01998-5
中图分类号
S7 [林业];
学科分类号
0829 ; 0907 ;
摘要
The aim of the present work was to investigate whether it is possible to use ground pine needles as formaldehyde-scavenging filler for urea-formaldehyde resin in the production of plywood. The scope of the research included determinations of both optimal amount of introduced filler and the effect of its modification (silanization, hydrothermal and alkaline treatments). Properties of adhesives such as viscosity, gel time and pH were investigated and their morphology was assessed using scanning electron microscopy. The manufactured plywood panels were tested in terms of their wet shear strength, tendency to delamination in varying conditions and formaldehyde emission. It was found that the addition of pine needles lowers the pH and reduces gel time of the adhesive. Moreover, it was shown that despite the significant reduction in formaldehyde emission, the addition of non-modified needles causes a decrease in bonding quality of plywood. Based on the results, 10 parts by weight of needles per 100 parts by weight of resin can be considered as an optimal loading. The use of ground needles modified hydrothermally and with silane allows to minimize the negative effect on the strength of glue lines and leads to further reduction of formaldehyde emission. Therefore, it can be concluded that pine needle powder has strong potential for the application as a formaldehyde-scavenging filler for urea-formaldehyde adhesive in plywood production.
引用
收藏
页码:147 / 158
页数:12
相关论文
共 50 条
[31]   Natural Additive for Reducing Formaldehyde Emissions in Urea-Formaldehyde Resins [J].
Pereira, Flavio ;
Pereira, Joao ;
Paiva, Nadia ;
Ferra, Joao ;
Martins, Jorge Manuel ;
Magalhaes, Fernao D. ;
Carvalho, Luisa .
JOURNAL OF RENEWABLE MATERIALS, 2016, 4 (01) :41-46
[32]   Research Progress and Prospect of Inorganic Filler for Urea-formaldehyde Resin Adhesive [J].
Tang, Qingguo ;
Wang, Fei ;
Shao, Hongxia ;
Ding, Yan .
ADVANCE IN ECOLOGICAL ENVIRONMENT FUNCTIONAL MATERIALS AND ION INDUSTRY III, 2012, 427 :148-+
[33]   Effect of a static magnetic field of 7 mT on formaldehyde biodegradation in industrial wastewater from urea-formaldehyde resin production by activated sludge [J].
Lebkowska, Maria ;
Narozniak-Rutkowska, Anna ;
Pajor, Elzbieta .
BIORESOURCE TECHNOLOGY, 2013, 132 :78-83
[34]   Reduction of formaldehyde emission from plywood using composite resin composed of resorcinol-formaldehyde and urea-modified scallop shell nanoparticles [J].
Yamanaka, Shinya ;
Magara, Kohei ;
Hirabayashi, Yasushi ;
Fujimoto, Toshiyuki ;
Kuga, Yoshikazu .
WOOD SCIENCE AND TECHNOLOGY, 2017, 51 (02) :297-308
[35]   Manufacturing Particleboard Using Hemp Shiv and Wood Particles with Low Free Formaldehyde Emission Urea-Formaldehyde Resin [J].
Li, Xiaoping ;
Wang, Siqun ;
Du, Guanben ;
Wu, Zhangkang ;
Gong, Yingchun .
FOREST PRODUCTS JOURNAL, 2014, 64 (5-6) :187-191
[36]   Substitution of urea-formaldehyde by renewable phenolic compound for environmentally appropriate production of particleboards [J].
Correa Furtini, Ana Carolina ;
Silva Brito, Flavia Maria ;
Guimaraes Junior, Mario ;
Osajima Furtini, Josy Anteveli ;
Alves Pinto, Luciana de Matos ;
Protasio, Thiago de Paula ;
Mendes, Lourival Marin ;
Guimaraes Junior, Jose Benedito .
ENVIRONMENTAL SCIENCE AND POLLUTION RESEARCH, 2022, 29 (44) :66562-66577
[37]   STUDY OF MECHANICAL PROPERTIES OF UREA-FORMALDEHYDE THERMOSETS REINFORCED BY PINE NEEDLE POWDER [J].
Singha, Amer S. ;
Thakur, Vijay Kumar .
BIORESOURCES, 2009, 4 (01) :292-308
[38]   Improved Plywood Strength and Lowered Emissions from Soybean Meal/Melamine Urea-Formaldehyde Adhesives [J].
Gao, Qiang ;
Shi, Sheldon ;
Zhang, Shifeng ;
Li, Jianzhang ;
Liang, Kaiwen .
FOREST PRODUCTS JOURNAL, 2011, 61 (08) :688-693
[39]   Study on surface grafting of hydroxyapatite and its influence on the properties of urea-formaldehyde resin [J].
Zheng, Wenyu ;
Hou, Tianle ;
Fan, Jinhua ;
Wang, Guangyu ;
Cai, Chunyan ;
Li, Yuxuan ;
Guanchang, Jinsui ;
Liu, Chunyu ;
Chen, Yuzhu ;
Xiao, Hui .
INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2024, 132
[40]   Influence of Acrylamide Copolymerization of Urea-Formaldehyde Resin Adhesives to Their Chemical Structure and Performance [J].
Abdullah, Zaimatul Aqmar ;
Park, Byung-Dae .
JOURNAL OF APPLIED POLYMER SCIENCE, 2010, 117 (06) :3181-3186