Preparation, Structure and Properties of Epoxy/Carbonyl Iron Powder Wave-Absorbing Foam for Electromagnetic Shielding

被引:1
作者
Liu, Xiaoli [1 ,2 ]
Huang, Hao [1 ,2 ]
Lu, Haijun [1 ,2 ]
机构
[1] AVIC Beijing Aeronaut Mfg Technol Res Inst, Composite Technol Ctr, Beijing 101300, Peoples R China
[2] AECC Beijing Inst Aeronaut Mat, Natl Key Lab Adv Composites, Beijing 100095, Peoples R China
关键词
carbonyl iron powder; absorber; foam; reflectivity; BUTADIENE RUBBER/CLAY NANOCOMPOSITES; CARBONYL IRON; MICROWAVE-ABSORPTION; COMPOSITES; DESIGN;
D O I
10.3390/polym16050698
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
The application of absorbing materials for electromagnetic shielding is becoming extensive, and the use of absorbents is one of the most important points of preparing absorbing foam materials. In this work, epoxy resin was used as the matrix and carbonyl iron powder (CIP) was used as the absorbent, and the structural absorbing foam materials were prepared by the ball mill dispersion method. Scanning electron microscopy showed that the CIP was evenly dispersed in the resin matrix. The foam structures formed at pre-polymerization times of 10 min, 30 min and 50 min were analyzed, and it was found that the cell diameter decreased from 0.47 mm to 0.31 mm with the increase in the pre-polymerization time. The reflectivity of the frontal and reverse sides of the foam gradually tends to be unified at frequencies of 2-18 GHz. When the CIP content increased from 30 wt% to 70 wt%, the cell diameter increased from 0.32 mm to 0.4 mm, and the uniformity of CIP distribution deteriorated. However, with the increase in the CIP content, the absorption properties of the composite materials were enhanced, and the absorption frequency band broadened. When the CIP content reached 70 wt%, the compression strength and modulus of the foam increased to 1.32 MPa and 139.0 MPa, respectively, indicating a strong ability to resist deformation.
引用
收藏
页数:11
相关论文
共 33 条
  • [1] Bioinspired design of nitrile-butadiene rubber/montmorillonite nanocomposites with hydrogen bond interactions leading to highly effective reinforcement
    Chen, Zilong
    Wang, Weichao
    Li, Jian
    Lin, Jun
    Li, Fanzhu
    Zhang, Liqun
    He, Shaojian
    [J]. POLYMER, 2023, 277
  • [2] Overview of MXene and conducting polymer matrix composites for electromagnetic wave absorption
    Dai, Bo
    Ma, Yong
    Dong, Feng
    Yu, Jia
    Ma, Mingliang
    Thabet, Hamdy Khamees
    El-Bahy, Salah M.
    Ibrahim, Mohamed M.
    Huang, Mina
    Seok, Ilwoo
    Roymahapatra, Gourisankar
    Naik, Nithesh
    Xu, Ben Bin
    Ding, Jianxu
    Li, Tingxi
    [J]. ADVANCED COMPOSITES AND HYBRID MATERIALS, 2022, 5 (02) : 704 - 754
  • [3] Oblique incidence performance of radar absorbing honeycombs
    Feng, Jiang
    Zhang, Yichen
    Wang, Peng
    Fan, Hualin
    [J]. COMPOSITES PART B-ENGINEERING, 2016, 99 : 465 - 471
  • [4] Folgueras LD, 2010, J AEROSP TECHNOL MAN, V2, P63
  • [5] Rational design of mesoporous MnO2 microwave absorber with tunable microwave frequency response
    He, Gaihua
    Duan, Yuping
    Pang, Huifang
    Zhang, Xuefeng
    [J]. APPLIED SURFACE SCIENCE, 2019, 490 : 372 - 382
  • [6] Nitrile butadiene rubber/clay nanocomposites cured and reinforced by copper sulfate pentahydrate
    He, Shaojian
    Li, Jian
    Zhang, Xiaoming
    Chen, Zilong
    Zhou, Hongfu
    Pang, Ce
    Weng, Yunxuan
    Lin, Jun
    [J]. JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2023, 22 : 2338 - 2342
  • [7] A novel method to prepare acrylonitrile-butadiene rubber/clay nanocomposites by compounding with clay gel
    He, Shaojian
    He, Tengfei
    Wang, Jiaqi
    Wu, Xiaohui
    Xue, Yang
    Zhang, Liqun
    Lin, Jun
    [J]. COMPOSITES PART B-ENGINEERING, 2019, 167 : 356 - 361
  • [8] Surface structural engineering of carbonyl iron powder for enhancing microwave absorption and anti-oxidation performance
    Huang, Ming-Lu
    Luo, Cheng-Long
    Sun, Chang
    Zhao, Kun-Yan
    Ou, Yingqing
    Wang, Ming
    [J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2024, 178 : 201 - 209
  • [9] Recent Progresses of High-Temperature Microwave-Absorbing Materials
    Jia, Zirui
    Lin, Kejun
    Wu, Guanglei
    Xing, Hui
    Wu, Hongjing
    [J]. NANO, 2018, 13 (06)
  • [10] Electromagnetic interference shielding nature of PVDF-carbonyl iron composites
    Joseph, Nina
    Sebastian, Mailadil Thomas
    [J]. MATERIALS LETTERS, 2013, 90 : 64 - 67