Analysis of Microstructure and Mechanical Properties of AZ31B Thick Plate Magnesium Alloy Stir Friction Welded Joints

被引：1

作者：

Pu, Jiafei ^{[1
,2
]}

Grigorievicth, Bondarev Sergii ^{[2
]}

Wang, Hongfeng ^{[1
]}

Liu, Shengrong ^{[1
]}

Song, Weiwei ^{[1
]}

Jiang, Di ^{[1
]}

Ge, Xiaole ^{[1
]}

Shouzhen, Cao ^{[1
]}

Dong, Qi ^{[1
,2
]}

机构：

[1] Huangshan Univ, Coll Mech & Elect Engn, Huangshan City, Anhui, Peoples R China

[2] Sumy Natl Agr Univ, Fac Engn & Technol, Sumy, Ukraine

来源：

INTEGRATED FERROELECTRICS | 2023年 / 236卷 / 01期

基金：

中国博士后科学基金;

关键词：

Friction stir welding; microstructure; tensile strength; impact resistance;

D O I：

10.1080/10584587.2023.2194828

中图分类号：

TM [电工技术]; TN [电子技术、通信技术];

学科分类号：

0808 ; 0809 ;

摘要：

Welding of 10 mm thick AZ31B magnesium alloy by stir friction welding technique. The effects of process parameters on the microstructure, tensile strength and impact resistance of the joints were analyzed. The results showed that the joints were formed with good quality and no obvious defects, and the joints were fine-grained and accompanied by grain dislocations. The grain dislocation in the hot machine influence zone is more obvious there is a dense grain dislocation zone, and the distribution is not uniform. When the spindle speed is 800 and 1000 rpm, respectively, the best impact resistance of the welded joint impact work is 8.02 J, which is about 94.2% of the impact resistance of AZ31B magnesium alloy base material. When the spindle speed is 1000r/min and the welding speed is 150 mm/min, the tensile strength of the welded joint is the largest, reaching 85.8% of the base material and the post-break elongation is 1.9 times that of the base material. Thick plate magnesium alloy plate welded joints overall performance is not uniform, welded plate bottom mechanical properties of the worst, weld core area doped magnesium alloy oxide, joint tensile fracture crack source from the bottom of the plate to the weld surface expansion.