Comparative Study of the Physico-Chemical Properties of Sorbents Based on Natural Bentonites Modified with Iron (III) and Aluminium (III) Polyhydroxocations

A comparative study of the physicochemical properties of natural bentonite clays of Pogodayevo (Republic of Kazakhstan, mod. 1) and Dash-Salakhli (Republic of Azerbaijan, mod. 2) deposits and modification of the bentonite clay with polyhydroxocations of iron (III) and aluminium (III). The amount of bentonite in the concentration of iron (aluminum) was 5 mmol Me3+/g. It was established that the modification of natural bentonites using polyhydroxocations of iron (III) (mod. 1_Fe_5-c, mod. 2_Fe_5-c) and aluminum (III) (mod. 1_Al_5-c, mod. 2_Al_5-c) by the method of "co-precipitation" leads to a change in their chemical composition, structural and sorption properties. The results showed that hydroxy-aluminum cations ([Al3O4(OH)24(H2O)12]7+) and poly-hydroxyl-Fe or polyoxo-Fe were intercalated into clay layers, which led to an increase in the values of d001 and specific surface areas compared to those of the original bentonite, from 37 to 120 m2/g for the Pogodaevo bentonite and from 51 to 172 m2/g respectively, for bentonite from the Dash-Salakhli deposit. It is shown that modified sorbents based on natural bentonite are finely porous objects with a predominance of pores of 1.5-8.0 nm in size. As a result, there is a significant increase in the specific surface area of sorbents. Modification of bentonite with polyhydroxocations of iron (III) and aluminum (III) by the "co-precipitation" method also leads to an increase in the sorption capacity of the sorbents obtained with respect to nickel (II) cations. Modified bentonites were used for the adsorption of Ni (II) ions from the model solution. Ni (II) was absorbed in a neutral pH solution. The study of equilibrium adsorption showed that the data are in good agreement with the Langmuir isotherm model. The maximum adsorption capacity of the Ni (II) obtained from the Langmuir equation was 25.0 mg/g (mod. 1_Al_5-c), 18.2 mg/g (mod. 2_Al_5-c) for Al-bentonite and 16.7 mg/g (mod. 1_Fe_5-c), 10.1 (mod. 2_Fe_5-c) for Fe-bentonite. The kinetics of adsorption is considered. The high content of Al-OH anion exchange centers in them determines the higher sorption activity of Al-modified bentonites.