Effects of Nb microalloying on the magnetic properties and microstructure of Fe-Si-B-P-Cu-Nb nanocrystalline alloys prepared with pure and industrial raw materials

被引：8
作者：
Zheng, Junwei [1 ,2 ]
Ding, Qian [1 ,2 ]
He, Aina [2 ,3 ]
Dong, Yaqiang [2 ,3 ]
Xie, Lei [2 ]
Li, Xubin [1 ,2 ]
Liu, Xincai [1 ]
Li, Jiawei [2 ,3 ]
机构：
[1] Ningbo Univ, Fac Mat Sci & Chem Engn, Ningbo 315211, Peoples R China
[2] Chinese Acad Sci, Ningbo Inst Mat Technol & Engn, Ningbo 315201, Peoples R China
[3] Univ Chinese Acad Sci, Beijing 100049, Peoples R China
来源：
JOURNAL OF ALLOYS AND COMPOUNDS | 2023年 / 934卷
关键词：
Nanocrystalline alloy; Nb; Industrial raw materials; Magnetic properties; Domain structure; BULK METALLIC GLASSES; SURFACE CRYSTALLIZATION; THERMAL-STABILITY; HEAT;
D O I：
10.1016/j.jallcom.2022.167886
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
Fe-based nanocrystalline alloys with high saturation magnetic flux density (Bs) and low coercivity (Hc) are highly desirable, especially if they can be prepared with industrial raw materials (IRMs). Here, Fe82.3Si4B9P4Cu0.7 and Fe82.3Si4B9P3Cu0.7Nb1 nanocrystalline ribbons were prepared with IRMs and pure raw materials (PRMs). It was found that Nb microalloying broadens the annealing process window of the rib-bons due to the suppressed precipitation of Fe(B, P) phase. In addition, the soft magnetic properties of the Fe82.3Si4B9P3Cu0.7Nb1 ribbons prepared with IRMs are insensitive to impurities and surface-crystallized layer. Compared to the PRMs-prepared ribbons, the IRMs increase the Hc of the Nb-free ribbons, whereas having little effect on the Hc of the Nb-doped ribbons with dendritic-crystallites in the surface layer. These results originate from the former forming coarse alpha-Fe grains and narrow magnetic domains, while the latter mainly forming fine alpha-Fe grains and broad magnetic domains. This work provides a valuable reference for the development and industrialization of nanocrystalline alloys with high Bs and low Hc.(c) 2022 Elsevier B.V. All rights reserved.
引用
收藏
页数：9
相关论文
共 41 条
  • [41] Partitioning of Co during crystallisation of Fe-Co-Nb-B(-Cu) amorphous alloys
    Zhang, Y
    Blazquez, JS
    Conde, A
    Warren, PJ
    Cerezo, A
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 353 (1-2): : 158 - 163
12345