Effect of alternating magnetic fields on hot tearing susceptibility of Mg-4Zn-1.5Ca alloy

被引：8
作者：
Bai, Shengwei [1 ,2 ]
Wang, Feng [1 ,2 ]
Du, Xudong [1 ,2 ]
Wang, Wei [2 ,3 ]
Wang, Zhi [1 ,2 ]
Zhou, Le [1 ,2 ]
Mao, Pingli [1 ,2 ]
Liu, Zheng [1 ,2 ]
机构：
[1] Shenyang Univ Technol, Sch Mat Sci & Engn, Shenyang 110870, Peoples R China
[2] Key Lab Magnesium Alloys & Proc Technol Liaoning, Shenyang 110870, Peoples R China
[3] Shenyang Univ Technol, Sch Sci, Shenyang, Peoples R China
来源：
MATERIALS SCIENCE AND TECHNOLOGY | 2023年 / 39卷 / 01期
关键词：
Mg-Zn-Ca alloy; low-frequency alternating magnetic fields; hot tearing susceptibility; solidification behaviour; microstructure; MECHANICAL-PROPERTIES; ALUMINUM-ALLOYS; MICROSTRUCTURE; REFINEMENT; ELEMENTS; CRACKING;
D O I：
10.1080/02670836.2022.2100605
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In the present work, the effect of low-frequency alternating magnetic fields (AMFs) of different strengths on hot tearing susceptibility (HTS) and solidification behaviour of the Mg-4Zn-1.5Ca alloy was investigated. The results revealed that the application of AMFs during the solidification narrowed the solidification temperature range of the Mg-4Zn-1.5Ca alloy, thereby reducing the HTS of the material. In addition, the presence of the AMF-inhibited dendritic growth refined the alloy microstructure and enhanced convection in the melt, which led to a decrease in the HTS. The HTS of the Mg-4Zn-1.5Ca alloy was the smallest when the AMF of 15 A (15 Hz) was applied. However, once the current increased to 20 A, excessive Joule heat was generated in the melt, which coarsened the microstructure and increased the HTS of the alloy.
引用
收藏
页码：50 / 61
页数：12
相关论文
共 41 条
[1]  
Abrams H., 1971, Metallography, V4, P59, DOI 10.1016/0026-0800(71)90005-X
[2]  
[Anonymous], 2006, MAGNESIUM ALLOYS THE
[3]  
[Anonymous], 1979, SOLIDIFICATION CASTI
[4]   A modified hot tearing criterion for direct chill casting of aluminium alloys [J].
Bai, Q. L. ;
Liu, J. C. ;
Li, H. X. ;
Du, Q. ;
Katgerman, L. ;
Zhang, J. S. ;
Zhuang, L. Z. .
MATERIALS SCIENCE AND TECHNOLOGY, 2016, 32 (08) :846-854
[5]   Effect of Ca Content on Hot Tearing Susceptibility of Mg-4Zn-xCa-0.3Zr (x=0.5, 1, 1.5, 2) Alloys [J].
Bai, Shengwei ;
Wang, Feng ;
Wang, Zhi ;
Leng, Feng ;
Liu, Zheng ;
Mao, Pingli .
INTERNATIONAL JOURNAL OF METALCASTING, 2021, 15 (04) :1298-1308
[6]  
Ban CY., 2002, FUNDAMENTAL STUDY SO
[7]   Onset of Hot Tearing in Ternary Mg-Al-Sr Alloy Castings [J].
Cao, G. ;
Haygood, I. ;
Kou, S. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2010, 41A (08) :2139-2150
[8]   Hot-Tearing Susceptibility of Ternary Mg-Al-Sr Alloy Castings [J].
Cao, G. ;
Zhang, C. ;
Cao, H. ;
Chang, Y. A. ;
Kou, S. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2010, 41A (03) :706-716
[9]   Mechanical properties of magnesium alloys for medical application: A review [J].
Chen, Junxiu ;
Tan, Lili ;
Yu, Xiaoming ;
Etim, Iniobong P. ;
Ibrahim, Muhammad ;
Yang, Ke .
JOURNAL OF THE MECHANICAL BEHAVIOR OF BIOMEDICAL MATERIALS, 2018, 87 :68-79
[10]   Effect of Al content on hot tearing behaviour of Mg-xAl-2Ca-2Sm alloys [J].
Chen, Yanhong ;
Wang, Liping ;
Feng, Yicheng ;
Wang, Lei ;
Guo, Erjun .
MATERIALS SCIENCE AND TECHNOLOGY, 2019, 35 (01) :116-126
12345