Area effect during the fracture process of high-Niobium-Titanium-Aluminum alloys under continuous tension loading-unloading

被引:0
作者
Zhong, Mingjie [1 ]
Lin, Youzhi [1 ,2 ]
机构
[1] Zhanjiang Univ Sci & Technol, Zhanjiang, Peoples R China
[2] Texas A&M Univ, Artie McFerrin Dept Chem Engn, College Stn, TX 77843 USA
关键词
high-Niobium-Titanium-Aluminum alloys; tension loading-unloading; area effect; fracture stress; damage mechanism; HIGH-NB; MECHANICAL-PROPERTIES; MICROSTRUCTURE EVOLUTION; TIAL ALLOYS; BEHAVIOR; TOUGHNESS;
D O I
10.3389/fmats.2023.1214873
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Based on the extracted results of the continuous tension loading-unloading testing, and observations of the corresponding cracks and fracture surfaces for the high-Niobium-Titanium-Aluminum alloys, both tensile damage and fracture mechanism were systematically studied. From the acquired results, it was demonstrated that the continuous tension loading-unloading did not affect the elastic modulus of the alloy. However, it decreased in fracture stress, fracture strain, and fracture work per unit area, and increased in irreversible strain. This result shows that the irreversible strain is not mainly caused by the volume effect of microcracks, but by the plastic strain of the materials. Although the density of the micro-cracks produced by multi-loading and unloading was small, most of the micro-cracks were concentrated on a certain section area, which results in an obvious area effect caused by the damage of the microcrack. In addition, the further propagation of the main crack under lower re-loading stress was not caused by the application of higher normal stress but by the residual tensile stress, which depends on the deterioration of the material at the crack tip during the unloading process of the alloy. These small amounts of microcracks are usually concentrated on the cross-sectional area, and the area effect caused by the microcracks damage is also obvious, which leads to a reduction of the fracture performance. Therefore, the area effect ultimately induces a decrease in fracture stress.
引用
收藏
页数:9
相关论文
共 38 条
[31]   Effects of grain size and precipitated phases on mechanical properties in TiAl gradient materials [J].
Wang, Qi ;
Chen, Ruirun ;
Yang, Yong ;
Guo, Jingjie ;
Su, Yanqing ;
Ding, Hongsheng ;
Fu, Hengzhi .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2018, 731 :634-641
[32]   Effect of heat treatment and thermomechanical processing on microstructure and tensile property of Ti-44Al-8Nb-0.2W-0.2B-0.5Y alloy [J].
Wang, Xiao-peng ;
Kong, Fan-tao ;
Cao, Xiao-ping ;
Zhang, Shu-zhi ;
Zhang, Chang-jiang ;
Chen, Yu-yong .
CHINA FOUNDRY, 2020, 17 (06) :447-454
[33]   Creep-Induced Phase Instability and Microstructure Evolution of a Nearly Lamellar Ti-45Al-8.5Nb-(W, B, Y) Alloy [J].
Wang, Xuyang ;
Yang, Jieren ;
Hu, Rui ;
Gao, Zitong ;
Li, Jinguang ;
Fu, Hengzhi .
ACTA METALLURGICA SINICA-ENGLISH LETTERS, 2020, 33 (12) :1591-1600
[34]  
Wei Sun, 2018, Applied Mechanics and Materials, V884, P29, DOI 10.4028/www.scientific.net/AMM.884.29
[35]  
Xu RR, 2019, RARE METAL MAT ENG, V48, P1406
[36]   Temperature-Dependence Corrosion Behavior of Ti6Al4V in the Presence of HCl [J].
Yu, Fei ;
Addison, Owen ;
Davenport, Alison .
FRONTIERS IN MATERIALS, 2022, 9
[37]  
Zhang XW, 2020, RARE METAL MAT ENG, V49, P138
[38]   Effect of microstructure on the fracture toughness of multi-phase high Nb-containing TiAl alloys [J].
Zhu, Bin ;
Xue, Xiangyi ;
Kou, Hongchao ;
Li, Xiaolei ;
Li, Jinshan .
INTERMETALLICS, 2018, 100 :142-150