Effect of temperature on corrosion fatigue behavior of Inconel Alloy 690TT steam generator tube

被引：7
|
作者：
Li, Z. H. [1 ]
Lu, Y. H. [1 ]
You, L. [2 ]
Zhang, X. F. [1 ]
Wang, L. [2 ]
Tian, D. H. [1 ]
Zhang, W. D. [1 ]
Shoji, T. [1 ]
机构：
[1] Univ Sci & Technol Beijing, Natl Ctr Mat Serv Safety, Beijing 100083, Peoples R China
[2] State Key Lab Nucl Power Safety Monitoring Technol, Shenzhen 518172, Peoples R China
来源：
CORROSION SCIENCE | 2024年 / 227卷
关键词：
Alloy 690TT tube; Corrosion fatigue; Temperature; Crack initiation; Fatigue life; CRACK-GROWTH-BEHAVIOR; LOW-CYCLE FATIGUE; DISSOLVED-OXYGEN; STAINLESS-STEEL; TIN INCLUSION; MECHANISMS;
D O I：
10.1016/j.corsci.2023.111741
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effect of temperature on corrosion fatigue behavior of actual Alloy 690TT steam generator (SG) tubes in water environments was studied. Results demonstrated that temperature had significant influence on the for-mation and initiation mechanism of persistent slip bands (PSBs), as well as the crack propagation mode and mechanism, in water environment. With the increase of temperature, the corrosion fatigue life of SG tube decreased, more fatigue cracks initiated along the PSBs, and the synergistic effect of slip dissolution and local plasticity accelerated fatigue crack propagation. Then, the evaluation model of temperature on corrosion fatigue life was established.
引用
收藏
页数：12
相关论文
共 50 条
  • [41] Crevice Corrosion Behavior of Alloy 690 in High-Temperature Aerated Chloride Solution
    Ning, Fangqiang
    Tan, Jibo
    Zhang, Ziyu
    Wang, Xiang
    Wu, Xinqiang
    Han, En-Hou
    Ke, Wei
    MATERIALS, 2022, 15 (15)
  • [42] Crevice corrosion behavior of Alloy 690 in high-temperature water
    Ning, Fangqiang
    Wu, Xinqiang
    Tan, Jibo
    JOURNAL OF NUCLEAR MATERIALS, 2019, 515 : 326 - 337
  • [43] Contact geometry and contact time effect on 690TT alloy/405 stainless steel impact-sliding fretting wear processes
    Mi, Xue
    Tang, Pan
    Zhang, Jun
    Bai, Xiao-ming
    Sun, Qi
    Zhu, Min-hao
    WEAR, 2025, 562
  • [44] ANALYSIS OF SURFACE OXIDE FILM FORMED ON ELETROPOLISHED ALLOY 690TT IN HIGH TEMPERATURE AND HIGH PRESSURE WATER WITH SEQUENTIALLY DISSOLVED HYDROGEN AND OXYGEN
    Zhang Zhiming
    Wang Jianqiu
    Han En-Hou
    Ke Wei
    ACTA METALLURGICA SINICA, 2015, 51 (01) : 85 - 92
  • [45] Effect of maximum stress intensity factor, loading mode, and temperature on corrosion fatigue cracking behavior of Inconel 617 in supercritical water
    Khan, Hasan Izhar
    Zhang, Naiqiang
    Xu, Weiqiao
    Zhu, Zhongliang
    Jiang, Dongfang
    Xu, Hong
    INTERNATIONAL JOURNAL OF FATIGUE, 2019, 118 : 22 - 34
  • [46] Crack Initiation Factor by Impact Fretting Wear at INCONEL Alloy for Steam Generator Tube in Nuclear Power Plants
    Park, Chi Yong
    Lee, Jeong Kun
    Kim, Tae Ryong
    Cho, Sun Young
    Jeon, Hyun Ik
    ADVANCED MATERIALS AND PROCESSING, 2007, 26-28 : 1269 - +
  • [47] CRACK GROWTH BEHAVIOR FOR STRESS CORROSION CRACKING OF 690 ALLOY IN HIGH TEMPERATURE WATER
    Dan Tichun
    Lue Zhanpeng
    Wang Jianqiu
    Han Enhou
    Shoji, Testuo
    Ke Wei
    ACTA METALLURGICA SINICA, 2010, 46 (10) : 1267 - 1274
  • [48] Effect of temperature on fretting wear behavior and mechanism of alloy 690 in water
    Lai, Ping
    Gao, Xiaochuan
    Tang, Lichen
    Guo, Xianglong
    Zhang, Lefu
    NUCLEAR ENGINEERING AND DESIGN, 2018, 327 : 51 - 60
  • [49] Effect of broaching on high-temperature fatigue behavior in notched specimens of INCONEL 718
    T. Connolley
    M. J. Starink
    P. A. S. Reed
    Metallurgical and Materials Transactions A, 2004, 35 : 771 - 783
  • [50] INFLUENCES OF TiN INCLUSION ON CORROSION AND STRESS CORROSION BEHAVIORS OF ALLOY 690 TUBE IN HIGH TEMPERATURE AND HIGH PRESSURE WATER
    Li Xiaohui
    Huang Fa
    Wang Jianqiu
    Han En-Hou
    Ke Wei
    ACTA METALLURGICA SINICA, 2011, 47 (07) : 847 - 852