The low cycle fatigue property, damage mechanism, and life prediction of additively manufactured Inconel 625: Influence of temperature

被引：4
|
作者：
Liu, Meng [1 ,2 ,3 ]
Cai, Yifang [1 ,2 ]
Wang, Quanyi [1 ,2 ]
Jiang, Yunqing [1 ,2 ]
Zou, Tongfei [1 ,2 ]
Wang, Yunru [1 ,2 ]
Li, Qingsong [3 ]
Pei, Yubing [3 ]
Zhang, Hong [1 ,2 ,3 ]
Liu, Yongjie [1 ,2 ]
Wang, Qingyuan [1 ,2 ,4 ]
机构：
[1] Sichuan Univ, Coll Architecture & Environm, Failure Mech & Engn Disaster Prevent & Mitigat, Key Lab Sichuan Prov, Chengdu, Peoples R China
[2] Sichuan Univ, Key Lab Deep Underground Sci & Engn, Minist Educ, Chengdu, Peoples R China
[3] Dongfang Turbine Co Ltd, State Key Lab Long Life High Temp Mat, Deyang, Peoples R China
[4] Chengdu Univ, Sch Architecture & Civil Engn, Chengdu, Peoples R China
来源：
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES | 2023年 / 46卷 / 10期
基金：
中国国家自然科学基金;
关键词：
additive manufacturing; failure mechanism; LCF; life prediction; microstructure evolution; NICKEL-BASED SUPERALLOY; ROOM-TEMPERATURE; DYNAMIC RECRYSTALLIZATION; DEFORMATION-BEHAVIOR; FRACTURE-BEHAVIOR; ENERGY DEPOSITION; CRACK INITIATION; SERRATED FLOW; STRAIN-ENERGY; DELTA-PHASE;
D O I：
10.1111/ffe.14106
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Symmetrical high-temperature low-cycle fatigue tests were performed in this study to examine the influence of temperature on the fatigue failure mechanism of the additively manufactured Inconel 625. According to the fracture analysis, cracks initiate from the crystallographic plane at room temperature. At 600 & DEG;C, oxidation of carbides leads to crack initiation. The strengthening effect of & gamma;& DPRIME; precipitation prevents crack propagating within the matrix. At 750 & DEG;C, the crack becomes transgranular propagating, as a consequence of & gamma;& DPRIME;-& delta; transformation. Geometrically necessary dislocations distribution on the fracture supports this result. Furthermore, a modified life prediction formula considering effect of temperature and strain amplitude was established. It was observed that the modified model predicted the fatigue life of the studied materials well in both test conditions.
引用
收藏
页码：3829 / 3845
页数：17
相关论文
共 50 条
  • [21] Influence of temperature on low-cycle fatigue behavior of inconel 625 nickel-based superalloy welding joint
    Chen, Lijia, 1600, Chinese Academy of Sciences (50):
  • [22] INFLUENCE OF HEAT TREATMENT ON THE MICROSTRUCTURAL PROPERTIES OF WIRE ARC ADDITIVELY MANUFACTURED INCONEL 625 ALLOY
    Thangapandian, N.
    Manivannan, R.
    Shanmugam, Ragavanantham
    Vivekananda, A. S.
    Rangarajan, V.
    PROCEEDINGS OF ASME 2023 INTERNATIONAL MECHANICAL ENGINEERING CONGRESS AND EXPOSITION, IMECE2023, VOL 4, 2023,
  • [23] High-Temperature Fatigue of Additively Manufactured Inconel 718: A Short Review
    Alfred, Samuel Onimpa
    Amiri, Mehdi
    JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 2025, 147 (01):
  • [24] Macroscale Property Prediction for Additively Manufactured IN625 from Microstructure Through Advanced Homogenization
    Saha, Sourav
    Kafka, Orion L.
    Lu, Ye
    Yu, Cheng
    Liu, Wing Kam
    INTEGRATING MATERIALS AND MANUFACTURING INNOVATION, 2021, 10 (03) : 360 - 372
  • [25] Macroscale Property Prediction for Additively Manufactured IN625 from Microstructure Through Advanced Homogenization
    Sourav Saha
    Orion L. Kafka
    Ye Lu
    Cheng Yu
    Wing Kam Liu
    Integrating Materials and Manufacturing Innovation, 2021, 10 : 360 - 372
  • [26] Remaining fatigue life prediction of additively manufactured Inconel 718 alloy based on in-situ SEM and deep learning
    Zhang, Yixu
    Wang, Ni
    Zhou, Jianli
    Wang, Hao
    Tang, Liang
    Zhang, Yuefei
    Zhang, Ze
    ENGINEERING FAILURE ANALYSIS, 2024, 163
  • [27] High-temperature tensile and high cycle fatigue properties of inconel 625 alloy manufactured by laser powder bed fusion
    Kim, Kyu-Sik
    Kang, Tae-Hoon
    Kassner, Michael E.
    Son, Kwang-Tae
    Lee, Kee-Ahn
    ADDITIVE MANUFACTURING, 2020, 35
  • [28] High-temperature high-cycle fatigue performance and machine learning-based fatigue life prediction of additively manufactured Hastelloy X
    Lei, Liming
    Li, Bo
    Wang, Haijie
    Huang, Guoqing
    Xuan, Fuzhen
    INTERNATIONAL JOURNAL OF FATIGUE, 2024, 178
  • [29] Quantitative analysis on low cycle fatigue damage: a microstructural model for the prediction of fatigue life
    Kim, HJ
    Lee, CS
    Park, SH
    Shin, DH
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 379 (1-2): : 210 - 217
  • [30] The low-cycle fatigue, fracture and life prediction of compacted graphite iron: Influence of temperature
    Zou, C. L.
    Chen, L. J.
    Pang, J. C.
    Wang, M.
    Qiu, Y.
    Li, S. X.
    Zhang, Z. F.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2019, 763
12345