The low cycle fatigue property, damage mechanism, and life prediction of additively manufactured Inconel 625: Influence of temperature

被引：5
作者：
Liu, Meng [1 ,2 ,3 ]
Cai, Yifang [1 ,2 ]
Wang, Quanyi [1 ,2 ]
Jiang, Yunqing [1 ,2 ]
Zou, Tongfei [1 ,2 ]
Wang, Yunru [1 ,2 ]
Li, Qingsong [3 ]
Pei, Yubing [3 ]
Zhang, Hong [1 ,2 ,3 ]
Liu, Yongjie [1 ,2 ]
Wang, Qingyuan [1 ,2 ,4 ]
机构：
[1] Sichuan Univ, Coll Architecture & Environm, Failure Mech & Engn Disaster Prevent & Mitigat, Key Lab Sichuan Prov, Chengdu, Peoples R China
[2] Sichuan Univ, Key Lab Deep Underground Sci & Engn, Minist Educ, Chengdu, Peoples R China
[3] Dongfang Turbine Co Ltd, State Key Lab Long Life High Temp Mat, Deyang, Peoples R China
[4] Chengdu Univ, Sch Architecture & Civil Engn, Chengdu, Peoples R China
来源：
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES | 2023年 / 46卷 / 10期
基金：
中国国家自然科学基金;
关键词：
additive manufacturing; failure mechanism; LCF; life prediction; microstructure evolution; NICKEL-BASED SUPERALLOY; ROOM-TEMPERATURE; DYNAMIC RECRYSTALLIZATION; DEFORMATION-BEHAVIOR; FRACTURE-BEHAVIOR; ENERGY DEPOSITION; CRACK INITIATION; SERRATED FLOW; STRAIN-ENERGY; DELTA-PHASE;
D O I：
10.1111/ffe.14106
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Symmetrical high-temperature low-cycle fatigue tests were performed in this study to examine the influence of temperature on the fatigue failure mechanism of the additively manufactured Inconel 625. According to the fracture analysis, cracks initiate from the crystallographic plane at room temperature. At 600 & DEG;C, oxidation of carbides leads to crack initiation. The strengthening effect of & gamma;& DPRIME; precipitation prevents crack propagating within the matrix. At 750 & DEG;C, the crack becomes transgranular propagating, as a consequence of & gamma;& DPRIME;-& delta; transformation. Geometrically necessary dislocations distribution on the fracture supports this result. Furthermore, a modified life prediction formula considering effect of temperature and strain amplitude was established. It was observed that the modified model predicted the fatigue life of the studied materials well in both test conditions.
引用
收藏
页码：3829 / 3845
页数：17
相关论文
共 84 条
[21]   Low cycle fatigue behavior of direct metal laser sintered Inconel alloy 718 [J].
Gribbin, Sean ;
Bicknell, Jonathan ;
Jorgensen, Luke ;
Tsukrov, Igor ;
Knezevic, Marko .
INTERNATIONAL JOURNAL OF FATIGUE, 2016, 93 :156-167
[22]   Tensile deformation behavior of a nickel based superalloy at different temperatures [J].
Hrutkay, K. ;
Kaoumi, D. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 599 :196-203
[23]   Microstructural evolution and anisotropic mechanical properties of Inconel 625 superalloy fabricated by directed energy deposition [J].
Hu, Yunlong ;
Lin, Xin ;
Li, Yunlong ;
Ou, Yongchao ;
Gao, Xuehao ;
Zhang, Qiang ;
Li, Wei ;
Huang, Weidong .
JOURNAL OF ALLOYS AND COMPOUNDS, 2021, 870
[24]   Benchmark experiments and characteristic cyclic plasticity deformation [J].
Jiang, Yanyao ;
Zhang, Jixi .
INTERNATIONAL JOURNAL OF PLASTICITY, 2008, 24 (09) :1481-1515
[25]   High resolution electron back-scatter diffraction analysis of thermally and mechanically induced strains near carbide inclusions in a superalloy [J].
Karamched, Phani S. ;
Wilkinson, Angus J. .
ACTA MATERIALIA, 2011, 59 (01) :263-272
[26]   SERRATED FLOW IN INCONEL-625 [J].
KIM, IS ;
CHATURVEDI, MC .
TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1987, 28 (03) :205-212
[27]   High-temperature tensile and high cycle fatigue properties of inconel 625 alloy manufactured by laser powder bed fusion [J].
Kim, Kyu-Sik ;
Kang, Tae-Hoon ;
Kassner, Michael E. ;
Son, Kwang-Tae ;
Lee, Kee-Ahn .
ADDITIVE MANUFACTURING, 2020, 35
[28]   Effect of anisotropy and texture on the low cycle fatigue behavior of Inconel 718 processed via electron beam melting [J].
Kirka, M. M. ;
Greeley, D. A. ;
Hawkins, C. ;
Dehoff, R. R. .
INTERNATIONAL JOURNAL OF FATIGUE, 2017, 105 :235-243
[29]   Fatigue Assessment of Inconel 625 Produced by Directed Energy Deposition from Miniaturized Specimens [J].
Klein Fiorentin, Felipe ;
Maciel, Duarte ;
Gil, Jorge ;
Figueiredo, Miguel ;
Berto, Filippo ;
de Jesus, Abilio .
METALS, 2022, 12 (01)
[30]   Microstructural degradation of polycrystalline superalloys from oxidized carbides and implications on crack initiation [J].
Kontis, Paraskevas ;
Collins, David M. ;
Wilkinson, Angus J. ;
Reed, Roger C. ;
Raabe, Dierk ;
Gault, Baptiste .
SCRIPTA MATERIALIA, 2018, 147 :59-63
123456789