Mechanistic insights into the selective adsorption of phosphorus from wastewater by MgO(100)-functionalized cellulose sponge

Metal oxides have remained state-of-the-art adsorbents for recovering phosphorus from aqueous solutions, but their practical application is still limited by their unsatisfactory adsorption capacities and selectivities in wastewater. Here, using MgO as a model metal oxide, the strategy of employing porous cellulose sponge to support metal oxides featuring exposed specific crystal facets was proposed to develop promising phosphate adsorbents. The phosphate ad-sorption isotherms and kinetics were measured and the phosphate adsorption mechanism was explored. The results show that cellulose sponge-supported MgO(100) (C-MgO(100)) has a saturation capacity of 28.3 mg P/g, over ten times higher than MgO(100) particles. Importantly, the phosphate adsorption properties of C-MgO(100) are almost not affected in wastewater, demonstrating its exceptional selectivity for phosphate adsorption. In contrast, the satura-tion capacity of MgO(111)-functionalized cellulose sponge is obviously declined in wastewater. Experimental together with theoretical analyses indicate that phosphate is chemically adsorbed on C-MgO(100) with obvious electrons trans-fer from the p-orbital of phosphate, and the adsorption energy of C-MgO(100) towards phosphate is maintained in the presence of coexisting anions. Ultimately, regeneration experiments reveal that a regenerant formulation composed of KOH (wt.1 %) and tap water is suitable for the regeneration of C-MgO(100) with >82.6 % phosphate desorption efficiencies after 5 cycles, further confirming its potential in practical application for the treatment of real water.