In vitro evaluation of fissure sealants'wear under erosive, abrasive and erosive/abrasive conditions

被引:1
|
作者
Hamza, B. [1 ]
Sekularac, M. [2 ]
Attin, T. [2 ]
Wegehaupt, F. J. [2 ]
机构
[1] Univ Zurich, Ctr Dent Med, Clin Orthodont & Pediat Dent, Plattenstr 11, CH-8032 Zurich, Switzerland
[2] Univ Zurich, Ctr Dent Med, Clin Conservat & Prevent Dent, CH-8032 Zurich, Switzerland
关键词
Fissure sealants; Material wear; Fillers; Erosive challenge; Abrasive challenge; FLUORIDE;
D O I
10.1007/s40368-022-00757-z
中图分类号
R78 [口腔科学];
学科分类号
1003 ;
摘要
Purpose To evaluate and compare the wear of selected resin-based fissure sealants with different compositions properties under erosive, abrasive, and erosive/abrasive conditions. Methods Forty-five samples of the following resin-based fissure sealants were prepared: Fissurit (fluoride free), Fissurit F (with fluoride), Fissurit FX (55 wt.% filler content), Grandio Seal (70 wt.% nano-filler content) and bovine enamel. Fifteen samples from each material were randomly allocated into three groups according to the wear condition they would be subjected to as follows: erosive condition (citric acid, 1 min, pH 2.3), abrasive condition (120 brushing strokes at 2 N, toothpaste slurry RDA value =69), and erosive/abrasive condition (combination of both). The wear challenges were repeated six times each day for 10 days. The material wear was measured using a stylus profilometer. Kruskal-Wallis and Conover's test was applied to compare the resulting material wear between the groups. Results Under erosive conditions, Grandio Seal and Fissurit FX showed statistically significantly the least material wear. Under abrasive and erosive/abrasive conditions, Grandio Seal showed statistically significantly the least material wear. Fissurit F showed statistically significantly the highest material wear under abrasive and erosive/abrasive conditions, after dental enamel (p < 0.05). Conclusion Higher filler content in sealants leads to better wear resistance. Incorporating fluoride into sealants seems to reduce their wear resistance at similar filler contents.
引用
收藏
页码:55 / 61
页数:7
相关论文
共 50 条
  • [31] Nondestructive testing for the integrity evaluation of erosive and abrasive boundary layers
    Meged, Y.
    JOURNAL OF TESTING AND EVALUATION, 2007, 35 (06) : 634 - 643
  • [32] The Effect of Daily Fluoride Mouth Rinsing on Enamel Erosive/Abrasive Wear in situ
    Stenhagen, K. R.
    Hove, L. H.
    Holme, B.
    Tveit, A. B.
    CARIES RESEARCH, 2013, 47 (01) : 2 - 8
  • [33] Erosive wear of borosilicate glass by low velocity unidirectional impact of abrasive spheres
    Mohajerani, A.
    Spelt, J. K.
    WEAR, 2011, 270 (11-12) : 866 - 875
  • [34] Effectiveness of resin-based materials against erosive and abrasive enamel wear
    Zhao, Xiaoyi
    Pan, Jie
    Zhang, Songmei
    Malmstrom, Hans S.
    Ren, Yan-Fang
    CLINICAL ORAL INVESTIGATIONS, 2017, 21 (01) : 463 - 468
  • [35] SOME OBSERVATIONS ON EROSIVE-ABRASIVE WEAR OF METALLIC SURFACES IN PARTICULAR GEOMETRIES
    BENCHAITA, MT
    TRIBOLOGY TRANSACTIONS, 1988, 31 (01): : 133 - 140
  • [36] THICK TI/TIN MULTILAYERED COATINGS FOR ABRASIVE AND EROSIVE WEAR-RESISTANCE
    LEYLAND, A
    MATTHEWS, A
    SURFACE & COATINGS TECHNOLOGY, 1994, 70 (01): : 19 - 25
  • [37] Effectiveness of resin-based materials against erosive and abrasive enamel wear
    Xiaoyi Zhao
    Jie Pan
    Songmei Zhang
    Hans S. Malmstrom
    Yan-Fang Ren
    Clinical Oral Investigations, 2017, 21 : 463 - 468
  • [38] Performance of polyimide and PTFE based composites under sliding, erosive and high stress abrasive conditions
    Kumar, Rahul
    Malaval, Bastien
    Antonov, Maksim
    Zhao, Gai
    TRIBOLOGY INTERNATIONAL, 2020, 147
  • [39] REACTIVITY OF METALS UNDER CONDITIONS OF EROSIVE WEAR
    MISRA, RDK
    BURSTEIN, GT
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 1985, 38 (03) : 198 - 206
  • [40] Abrasive and Erosive Wear Performance of Rare Earth Oxide Doped Ni/WC Coatings
    Purkayastha, Surajit
    Dwivedi, D. K.
    JOURNAL OF TRIBOLOGY-TRANSACTIONS OF THE ASME, 2014, 136 (01):