Effect of micro-galvanic corrosion on corrosion fatigue cracking of the weld joint of high strength bridge steel

被引：11
|
作者：
Li, Qi [1 ]
Yao, Qiong [2 ]
Sun, Liyang [1 ]
Ma, Hongchi [1 ]
Zhang, Chuang [2 ]
Wang, Ning [2 ]
机构：
[1] Univ Sci & Technol, Inst Adv Mat & Technol, Natl Mat Corros & Protect Data Ctr, Key Lab Corros & Protect MOE, Beijing 100083, Peoples R China
[2] Xichang Satellite Launch Ctr, Xichang 615000, Sichuan, Peoples R China
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2023年 / 170卷
基金：
中国国家自然科学基金;
关键词：
High-strength bridge steel; Marine atmosphere; Local electrochemical technique; Micro-galvanic corrosion; Corrosion fatigue failure; SCANNING KELVIN PROBE; E690; STEEL; FORCE MICROSCOPY; GROWTH-BEHAVIOR; CR; MICROSTRUCTURE;
D O I：
10.1016/j.ijfatigue.2023.107568
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The local electrochemical and corrosion fatigue cracking behavior of the weld joint of Q690qE high-strength bridge steel was investigated in simulated marine environment. It reveals the weld joint was vulnerable to corrosion fatigue failure in polluted marine atmosphere with the corrosion fatigue life considerably lower than that of parent metal. The micro-galvanic corrosion effect between CGHAZ and WM played a dominant role in the corrosion fatigue failure of the weld joint, leading to the final fracture mostly at CGHAZ. The micro-galvanic corrosion was caused by Volta potential variation among various subzones, which was evidenced by local electrochemical techniques.
引用
收藏
页数：15
相关论文
共 50 条
  • [1] Corrosion fatigue cracking behaviors of Q690qE high-strength bridge steel as a weld joint in simulated marine environment
    Lu, Cuiping
    Yao, Qiong
    Li, Ningning
    Sun, Liyang
    Dai, Wenhe
    Zhang, Chuang
    Ma, Hongchi
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2024, 47 (11) : 4341 - 4355
  • [2] Correlation of micro-galvanic corrosion behavior with corrosion rate in the initial corrosion process of dual phase steel
    Chen, Heng
    Lv, Zhaochong
    Lu, Lin
    Huang, Yunhua
    Li, Xiaogang
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2021, 15 : 3310 - 3320
  • [3] Numerical modeling of micro-galvanic corrosion
    Deshpande, Kiran B.
    ELECTROCHIMICA ACTA, 2011, 56 (04) : 1737 - 1745
  • [4] Susceptibility of rare-earth-magnesium alloys to micro-galvanic corrosion
    Coy, A. E.
    Viejo, F.
    Skeldon, P.
    Thompson, G. E.
    CORROSION SCIENCE, 2010, 52 (12) : 3896 - 3906
  • [5] Micro-galvanic corrosion during formation of epoxy coating
    Feng, Zhenliang
    Song, Guang-Ling
    Xu, Yuqing
    Zheng, Dajiang
    Chen, Xiaodong
    PROGRESS IN ORGANIC COATINGS, 2020, 147
  • [6] Gradient textures induce micro-galvanic corrosion on Mg
    Bai, Jing
    Sun, Chao
    Wang, Cheng
    Shao, Yi
    Meng, Jiao
    Dong, Qiangsheng
    Xue, Feng
    Chu, Chenglin
    JOURNAL OF ALLOYS AND COMPOUNDS, 2024, 1005
  • [7] Corrosion mechanism of eutectic high-entropy alloy induced by micro-galvanic corrosion in sulfuric acid solution
    Wei, Liang
    Qin, Weimin
    CORROSION SCIENCE, 2022, 206
  • [8] Hydrogen-Induced Cracking Caused by Galvanic Corrosion of Steel Weld in a Sour Environment
    Park, Jin Sung
    Lee, Jin Woo
    Kim, Sung Jin
    MATERIALS, 2021, 14 (18)
  • [9] Study on the effect of mischmetal (La,Ce) on the micro-galvanic corrosion of AZ91 alloy using multiscale methods
    Jia, Ruilin
    Yu, Shuang
    Li, Dan
    Zhang, Tao
    Wang, Fuhui
    Zhong, Cheng
    JOURNAL OF ALLOYS AND COMPOUNDS, 2019, 778 : 427 - 438
  • [10] A FEM model for investigation of micro-galvanic corrosion of Al alloys and effects of deposition of corrosion products
    Yin, Litao
    Jin, Ying
    Leygraf, Christofer
    Pan, Jinshan
    ELECTROCHIMICA ACTA, 2016, 192 : 310 - 318
12345