A numerical analysis on the behavior of CFRP laminates under biaxial loads

被引：2

作者：

Lucia Zumaquero, Patricia ^{[1
]}

Correa, Elena ^{[1
]}

Justo, Jesus ^{[1
]}

Paris, Federico ^{[1
]}

机构：

[1] Univ Seville, Sch Engn, Grp Elast & Strength Mat, Camino Descubrimientos S-N, Seville 41092, Spain

来源：

MECHANICS OF ADVANCED MATERIALS AND STRUCTURES | 2024年 / 31卷 / 07期

关键词：

Transverse failure; biaxial tests; FEM models; characterization test; cruciform coupon; GLASS-REINFORCED POLYESTER; SECONDARY TRANSVERSE LOAD; FIBER-MATRIX INTERFACE; INTERFIBER FAILURE; MICROSCOPIC OBSERVATIONS; STRESS STATES; COMPOSITES; TENSILE; COMPRESSION; DESIGN;

D O I：

10.1080/15376494.2022.2137887

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The study of the failure mechanisms of a composite material is essential for the efficient design of structures. The analysis of the effect of transverse biaxial loads, both at micromechanical and macromechanical level, is required for an integral vision of the whole mechanism of damage. In a previous work by the authors a transverse biaxial testing campaign was performed on cruciform specimens; in the present work a FEM model that successfully reproduces the coupons elastic state is presented in order to understand the failure occurrence and to make failure predictions avoiding the complexity of the experimental process.

引用

页码：1423 / 1435

页数：13

共 38 条

[21] Transverse biaxial tests on long fibre reinforced composites
Lucia Zumaquero, Patricia
Correa, Elena
Justo, Jesus
Paris, Federico
[J]. COMPOSITE STRUCTURES, 2022, 297
[22] Microscopical observations of interface cracks from inter-fibre failure under compression in composite laminates
Lucia Zumaquero, Patricia
Correa, Elena
Justo, Jesus
Paris, Federico
[J]. COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2018, 110 : 76 - 83
[23] Shape optimisation of a biaxially loaded cruciform specimen
Makris, A.
Vandenbergh, T.
Ramault, C.
Van Hemelrijck, D.
Lamkanfi, E.
Van Paepegem, W.
[J]. POLYMER TESTING, 2010, 29 (02) : 216 - 223
[24] Understanding the effect of anisotropy in composite materials on the performance of cruciform specimens
Moncy, A.
Castro, O.
Berggreen, C.
Stang, H.
[J]. COMPOSITE STRUCTURES, 2021, 273
[25] National Institute for Aviation Research,, 2011, CAMRP2010002 NAT I A
[26] Mixed-mode damage into a CGRP cruciform subjected to biaxial loading
Navarro-Zafra, J.
Curiel-Sosa, J. L.
Serna Moreno, M. C.
[J]. COMPOSITE STRUCTURES, 2015, 133 : 1093 - 1100
[27] Kinking of transversal interface cracks between fiber and matrix
Paris, Federico
Correa, Elena
Mantic, Vladislav
[J]. JOURNAL OF APPLIED MECHANICS-TRANSACTIONS OF THE ASME, 2007, 74 (04): : 703 - 716
[28] Fracture characterization of glass fiber composite laminate under experimental biaxial loading
Rashedi, A.
Sridhar, I.
Tseng, K. J.
[J]. COMPOSITE STRUCTURES, 2016, 138 : 17 - 29
[29] A study of the influence of a nearby fibre on the interface crack growth under transverse compression in composite materials
Sandino, Carlos
Correa, Elena
Paris, Federico
[J]. ENGINEERING FRACTURE MECHANICS, 2018, 193 : 1 - 16
[30] Failure strain and stress fields of a chopped glass-reinforced polyester under biaxial loading
Serna Moreno, M. C.
Martinez Vicente, J. L.
Lopez Cela, J. J.
[J]. COMPOSITE STRUCTURES, 2013, 103 : 27 - 33

← 1 2 3 4 →