Verification of stress transfer mechanism in fatigue crack growth under overload

被引：5
作者：
Wang, Chen [1 ]
Chen, Rong [1 ]
Guo, Su-Juan [1 ]
Zhu, Ming-Liang [1 ]
Xuan, Fu-Zhen [1 ]
机构：
[1] East China Univ Sci & Technol, Sch Mech & Power Engn, Key Lab Pressure Syst & Safety, Minist Educ, Shanghai 200237, Peoples R China
来源：
THEORETICAL AND APPLIED FRACTURE MECHANICS | 2023年 / 128卷
基金：
中国国家自然科学基金;
关键词：
Fatigue crack growth; Overload effect; Stress transfer; Crack tip blunting; Crack closure; MESH REFINEMENT; CLOSURE; PROPAGATION;
D O I：
10.1016/j.tafmec.2023.104104
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Cyclic plastic finite element modeling was carried out to investigate effect of overload on fatigue crack growth under blunting and no-blunting mechanisms at different overload ratios. The stress transfer mechanism was verified and was found more obvious in the case of crack blunting though its effect was time-limited. The level of crack closure varied periodically due to gradual relaxation of compressive residual stress during crack propagation. Both the overload plastic zone and the overload affected zone were linearly correlated with overload ratio, and an overload ratio value of 1.1 was the best choice for studying overload effect.
引用
收藏
页数：9
相关论文
共 50 条
  • [41] Fatigue crack growth under cyclic torsional loading
    Martins, Rui F.
    Ferreira, Luis
    Reis, Luis
    Chambel, Paulo
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2016, 85 : 56 - 66
  • [42] Overload induced fatigue crack growth and significance of retardation zone
    Pandey, RK
    Verma, BB
    ADVANCES IN FRACTURE RESEARCH, VOLS 1-6, 1997, : 1285 - 1296
  • [43] Effect of cyclic plastic strain on fatigue crack growth
    Vormwald, Michael
    INTERNATIONAL JOURNAL OF FATIGUE, 2016, 82 : 80 - 88
  • [44] Effect of crack flank holes on fatigue crack growth
    Neto, D. M.
    Cavaleiro, N.
    Sergio, E. R.
    Jesus, J.
    Camacho-Reyes, A.
    Antunes, F. V.
    INTERNATIONAL JOURNAL OF FATIGUE, 2023, 170
  • [45] Effect of single tensile overload on fatigue crack growth behavior of CP-Ti at negative load ratio
    Xie, Lin-qi
    Zhang, Peng
    He, Xiao-hua
    Zhou, Chang-yu
    INTERNATIONAL JOURNAL OF FATIGUE, 2021, 145
  • [46] ESTIMATION OF MINIMAL FATIGUE CRACK GROWTH RATE AFTER OVERLOAD-UNDERLOAD AT DIFFERENT STRESS RATIOS
    Yasniy, P., V
    Pyndus, Yu., I
    Fostyk, V. B.
    OPIR MATERIALIV I TEORIA SPORUD-STRENGTH OF MATERIALS AND THEORY OF STRUCTURES, 2015, (94): : 231 - 243
  • [47] Effect of single overload on fatigue crack growth in QSTE340TM steel and retardation model modification
    Lu, Yun-chao
    Yang, Feng-peng
    Chen, Te
    ENGINEERING FRACTURE MECHANICS, 2019, 212 : 81 - 94
  • [48] Evaluation of the overload effect on fatigue crack growth with the help of synchrotron XRD strain mapping
    Belnoue, Jonathan P.
    Jun, Tea-Sung
    Hofmann, Felix
    Abbey, Brian
    Korsunsky, Alexander M.
    ENGINEERING FRACTURE MECHANICS, 2010, 77 (16) : 3216 - 3226
  • [49] Study on the multi-scale online fatigue crack deformation and growth behaviors under overload in Q&P steel
    Gao, Hongli
    Zhan, Jingsong
    Li, Weirong
    Shang, Hongbin
    Lin, Zhiyuan
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2024, 47 (04) : 1172 - 1190
  • [50] Fatigue crack growth under mixed mode I-II loading with a single tensile overload at negative load ratios
    Xie, Lin-qi
    Zhou, Chang-yu
    Zhang, Peng
    He, Xiao-hua
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2022, 118
12345