Verification of stress transfer mechanism in fatigue crack growth under overload

被引：5
作者：
Wang, Chen [1 ]
Chen, Rong [1 ]
Guo, Su-Juan [1 ]
Zhu, Ming-Liang [1 ]
Xuan, Fu-Zhen [1 ]
机构：
[1] East China Univ Sci & Technol, Sch Mech & Power Engn, Key Lab Pressure Syst & Safety, Minist Educ, Shanghai 200237, Peoples R China
来源：
THEORETICAL AND APPLIED FRACTURE MECHANICS | 2023年 / 128卷
基金：
中国国家自然科学基金;
关键词：
Fatigue crack growth; Overload effect; Stress transfer; Crack tip blunting; Crack closure; MESH REFINEMENT; CLOSURE; PROPAGATION;
D O I：
10.1016/j.tafmec.2023.104104
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Cyclic plastic finite element modeling was carried out to investigate effect of overload on fatigue crack growth under blunting and no-blunting mechanisms at different overload ratios. The stress transfer mechanism was verified and was found more obvious in the case of crack blunting though its effect was time-limited. The level of crack closure varied periodically due to gradual relaxation of compressive residual stress during crack propagation. Both the overload plastic zone and the overload affected zone were linearly correlated with overload ratio, and an overload ratio value of 1.1 was the best choice for studying overload effect.
引用
收藏
页数：9
相关论文
共 50 条
  • [31] Experimental Study on the Fatigue Crack Growth and Overload Effect in Medium Density Polyethylene
    Qian, Yang-fan
    Yang, Feng-peng
    He, Hou-feng
    Du, He-yang
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2020, 29 (10) : 6681 - 6690
  • [32] Overload-induced retardation of fatigue crack growth in polycarbonate
    Fang, Qin-Zhi
    Wang, T. J.
    Li, H. M.
    INTERNATIONAL JOURNAL OF FATIGUE, 2008, 30 (08) : 1419 - 1429
  • [33] An approximation for the cyclic state of stress ahead of cracks and its implications under fatigue crack growth
    Madia, M.
    Beretta, S.
    ENGINEERING FRACTURE MECHANICS, 2011, 78 (03) : 573 - 584
  • [34] Fatigue crack growth in notched specimens: a numerical analysis
    Antunes, F., V
    Branco, R.
    Prates, P.
    Costa, J. D. M.
    FRATTURA ED INTEGRITA STRUTTURALE-FRACTURE AND STRUCTURAL INTEGRITY, 2019, 13 (48): : 666 - 675
  • [35] Probabilistic modeling of fatigue crack growth and experimental verification
    Li, Yi-Zhao
    Zhu, Shun-Peng
    Liao, Ding
    Niu, Xiao-Peng
    ENGINEERING FAILURE ANALYSIS, 2020, 118
  • [36] Reconsiderations of fatigue crack growth at negative stress ratios: Finite element analyses
    Benz, C.
    Sander, M.
    ENGINEERING FRACTURE MECHANICS, 2015, 145 : 98 - 114
  • [37] Material-independent stress ratio effect on the fatigue crack growth behavior
    Li, H. F.
    Yang, S. P.
    Zhang, P.
    Liu, Y. Q.
    Wang, B.
    Zhang, Z. F.
    ENGINEERING FRACTURE MECHANICS, 2022, 259
  • [38] Small time scale fatigue crack growth analysis
    Lu, Zizi
    Liu, Yongming
    INTERNATIONAL JOURNAL OF FATIGUE, 2010, 32 (08) : 1306 - 1321
  • [39] High temperature fatigue crack growth of Haynes 230
    Pataky, Garrett J.
    Sehitoglu, Huseyin
    Maier, Hans J.
    MATERIALS CHARACTERIZATION, 2013, 75 : 69 - 78
  • [40] Effect of kinematic hardening parameters on fatigue crack growth
    Borges, M. F.
    Antunes, F., V
    Prates, P. A.
    Branco, R.
    Cruces, A. S.
    Lopez-Crespo, P.
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2020, 106
12345