High-strength and energetic Al2Ti6Zr2Nb3Ta3 high entropy alloy containing a cuboidal BCC/B2 coherent microstructure

被引:30
作者
Jin, Dongming [1 ]
Wang, Zhenhua [1 ]
Yuan, Junhao [1 ]
Jiang, Beibei [2 ]
Yu, Fengyun [1 ]
Li, Jinfeng [3 ]
Wang, Qing [1 ]
机构
[1] Dalian Univ Technol, Dalian 116024, Peoples R China
[2] Guangdong Univ Technol, Anal & Test Ctr, Guangzhou 510006, Peoples R China
[3] China Acad Engn Phys, Inst Mat, Mianyang 621908, Peoples R China
基金
中国国家自然科学基金;
关键词
High entropy alloys; Microstructural stability; Coherent precipitation; Mechanical property; Combustion calorific capacity; RESOLVED SHEAR-STRESS; MECHANICAL-PROPERTIES; PRECIPITATION; NANOPARTICLES; STABILITY; TEMPERATURE; SUPERALLOY; BEHAVIOR;
D O I
10.1016/j.jallcom.2022.167546
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
The present work developed a novel high-strength and energetic Al2Ti6Zr2Nb3Ta3 high entropy alloy (HEA) containing a BCC/B2 coherent microstructure. The microstructural evolution of BCC/B2 with both the aging temperature (873 - 1073 K) and aging time (up to 200 h) was investigated, from which it was found that the cuboidal BCC nanoparticles are coherently-precipitated into the B2 matrix in 873 K-aged state due to a moderate lattice misfit (epsilon - - 0.76%). The increase of aging temperature could destroy the BCC/B2 coherency and accelerate the formation of brittle Zr5Al3 phase. Especially, the BCC/B2 microstructure exhibits an excellent thermal stability, as evidenced by the fact that these cuboidal BCC nanoprecipitates were not coarsened obviously at 873 K with the particle size from r - 10 nm in 24 h-aged state to r - 20 nm in 200 haged state. This alloy possesses prominent mechanical properties with high yield strength at both room temperature (Sigma YS = 1193 MPa) and elevated temperatures (1060 MPa at 873 K and 106 MPa at 1273 K), where the high strength was discussed in light of the precipitation strengthening mechanism. Importantly, the current alloy has an ultrahigh combustion calorific capacity with a value of 10240 Jmiddotg-1, showing a great potential to be used as novel high-performance energetic structural materials.(c) 2022 Elsevier B.V. All rights reserved.
引用
收藏
页数:11
相关论文
共 43 条
[1]  
[Anonymous], 1992, ASM HDB ALL PHAS DIA, p13B
[2]   PRECIPITATION HARDENING [J].
ARDELL, AJ .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1985, 16 (12) :2131-2165
[3]  
Argon A., 2007, Strengthening Mechanisms in Crystal Plasticity
[4]  
Brown L. M., 1971, STRENGTHENING METHOD, P10
[5]   Microstructural development in equiatomic multicomponent alloys [J].
Cantor, B ;
Chang, ITH ;
Knight, P ;
Vincent, AJB .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 375 :213-218
[6]   Pitting corrosion of the high-entropy alloy Co1.5CrFeNi1.5Ti0.5Mo0.1 in chloride-containing sulphate solutions [J].
Chou, Y. L. ;
Wang, Y. C. ;
Yeh, J. W. ;
Shih, H. C. .
CORROSION SCIENCE, 2010, 52 (10) :3481-3491
[7]   A novel microwave absorber of FeCoNiCuAl high-entropy alloy powders: Adjusting electromagnetic performance by ball milling time and annealing [J].
Duan, Yuping ;
Cui, Yulong ;
Zhang, Bin ;
Ma, Guojia ;
Wang Tongmin .
JOURNAL OF ALLOYS AND COMPOUNDS, 2019, 773 :194-201
[8]   Irradiation Resistance of Multicomponent Alloys [J].
Egami, T. ;
Guo, W. ;
Rack, P. D. ;
Nagase, T. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2014, 45A (01) :180-183
[9]   High-entropy alloys [J].
George, Easo P. ;
Raabe, Dierk ;
Ritchie, Robert O. .
NATURE REVIEWS MATERIALS, 2019, 4 (08) :515-534
[10]   ON CRITICAL RESOLVED SHEAR STRESS OF SOLID SOLUTIONS CONTAINING COHERENT PRECIPITATES [J].
GEROLD, V ;
HABERKORN, H .
PHYSICA STATUS SOLIDI, 1966, 16 (02) :675-&