Detrimental Effects of Chlorhexidine on Articular Cartilage Viability, Matrix, and Mechanics

Background: Chlorhexidine gluconate (CHG) solution is commonly used as an antiseptic irrigation for bacterial decontamination during orthopaedic surgery. Although the chondrotoxicity of CHG on articular cartilage has been reported, the full extent of CHG-related chondrotoxicity and its effects on the extracellular matrix and mechanical properties are unknown. Purpose: To investigate the in vitro effects of a single 1-minute CHG exposure on the viability, biochemical content, and mechanics of native articular cartilage explants. Study design: Controlled laboratory study. Methods: Articular cartilage explants (6 per group) were harvested from femoral condyles of the porcine stifle and sectioned at tidemark. Explants were bathed in CHG solution (0.05% CHG in sterile water) at varying concentrations (0% control, 0.01% CHG, and 0.05% CHG) for 1 minute, followed by complete phosphate-buffered saline wash and culture in chondrogenic medium. At 7 days after CHG exposure, cell viability, matrix content (collagen and glycosaminoglycan [GAG]), and compressive mechanical properties (creep indentation testing) were assessed. Results: One-minute CHG exposure was chondrotoxic to explants, with both 0.05% CHG (2.6% +/- 4.1%) and 0.01% CHG (76.3% +/- 8.6%) causing a decrease in chondrocyte viability compared with controls (97.5% +/- 0.6%; P < .001 for both). CHG exposure at either concentration had no significant effect on collagen content, while 0.05% CHG exposure led to a significant decrease in mean GAG per wet weight compared with the control group (2.6% +/- 1.7% vs 5.2% +/- 1.9%; P = .029). There was a corresponding weakening of mechanical properties in explants treated with 0.05% CHG compared with controls, with decreases in mean aggregate modulus (177.8 +/- 90.1 kPa vs 280.8 +/- 19.8 kPa; P < .029) and shear modulus (102.6 +/- 56.5 kPa vs 167.9 +/- 16.2 kPa; P < .020). Conclusion: One-minute exposure to CHG for articular cartilage explants led to dose-dependent decreases in chondrocyte viability, GAG content, and compressive mechanical properties. This raises concern for the risk of mechanical failure of the cartilage tissue after CHG exposure.