Microstructure, densification and mechanical properties of in situ TiBw/Ti2AlNb composites fabricated by spark plasma sintering

被引:5
作者
Wu, Tengfei [1 ]
Fan, Ronglei [1 ]
Wu, Yong [1 ]
Wu, Dipeng [1 ]
Yang, Jianlei [2 ]
Chen, Minghe [1 ]
机构
[1] Nanjing Univ Aeronaut & Astronaut, Coll Mech & Elect Engn, Nanjing 210016, Peoples R China
[2] Harbin Inst Technol, Sch Mat Sci & Engn, Weihai 264209, Peoples R China
基金
中国国家自然科学基金;
关键词
TEMPERATURE TENSILE PROPERTIES; TIBW/TI6AL4V COMPOSITES; MATRIX COMPOSITES; CREEP-BEHAVIOR; ALLOY; REINFORCEMENT; PARTICULATE; EVOLUTION;
D O I
10.1007/s10853-023-08540-1
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
TiB whisker-reinforced Ti2AlNb (TiBw/Ti2AlNb) composites with a network architecture were fabricated by the spark plasma sintering (SPS) technique at the temperature ranging from 950 to 1250 degrees C with the pressure range of 15-50 MPa for 5-30 min and followed by furnace cooling. The effects of SPS parameters and the volume fraction of TiB2 on the microstructure, densification, phase composition and mechanical properties of the sintered composites were studied in detail. The results revealed that the microstructure of TiBw/Ti2AlNb composites was related to the degree of in situ reaction, which was linked to sintering temperature, time, pressure and the volume fraction of TiB2. The TiBw/Ti2-AlNb composite exhibited the highest strength and plasticity at room temperature with the sintering process of 1200 degrees C/15 min/50 MPa/2.5 vol. % TiB2, and its ultimate tensile strength was nearly 240 MPa higher than that of SPS sintered Ti2AlNb-based alloy. However, its high-temperature mechanical properties were lower than those of SPS sintered Ti2AlNb-based alloy, which is due to the fact that the bonding strength between high-strength TiB whiskers and Ti2AlNb matrix was worse during hot deformation, the interface deboned before fracture, and the strengthening effect of TiBw decreased. Compared with the traditional TiBw-titanium alloys system, this work systematically discussed the influence of various parameters on the microstructure and mechanical properties of the composites under TiBw-Ti2AlNb-based alloys system, which can eventually enrich the application of network architecture in the field of powder metallurgy to improve the mechanical properties of materials and provide guidance for the optimization of process parameters.
引用
收藏
页码:8359 / 8378
页数:20
相关论文
共 48 条
[1]   The intermetallic Ti2AlNb [J].
Banerjee, D .
PROGRESS IN MATERIALS SCIENCE, 1997, 42 (1-4) :135-158
[2]   Part I. The microstructural evolution in Ti-Al-NbO plus Bcc orthorhombic alloys [J].
Boehlert, CJ ;
Majumdar, BS ;
Seetharaman, V ;
Miracle, DB .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1999, 30 (09) :2305-2323
[3]   Effect of cooling rate on phase transformation in Ti2AlNb alloy [J].
Bu, Z. Q. ;
Zhang, Y. G. ;
Yang, L. ;
Kang, J. M. ;
Li, J. F. .
JOURNAL OF ALLOYS AND COMPOUNDS, 2022, 893
[4]  
Cao D., 2023, PROCESS, DOI [10.13140/RG.2.2.26091.41760, DOI 10.13140/RG.2.2.26091.41760]
[5]  
Cao D, 2023, PROCESS
[6]   Nanoindentation measurement of core-skin interphase viscoelastic properties in a sandwich glass composite [J].
Cao, Dongyang ;
Malakooti, Sadeq ;
Kulkarni, Vijay N. ;
Ren, Yao ;
Lu, Hongbing .
MECHANICS OF TIME-DEPENDENT MATERIALS, 2021, 25 (03) :353-363
[7]   Room-temperature tensile and high-cycle-fatigue strength of fine TiB particulate-reinforced Ti-22Al-27Nb composites [J].
Emura, S ;
Yang, SJ ;
Hagiwara, M .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2004, 35A (09) :2971-2979
[8]   B2 grain size refinement and its effect on room temperature tensile properties of a Ti-22Al-27Nb orthorhombic intermetallic alloy [J].
Emura, S ;
Araoka, A ;
Hagiwara, M .
SCRIPTA MATERIALIA, 2003, 48 (05) :629-634
[9]   Titanium alloys and their machinability - A review [J].
Ezugwu, EO ;
Wang, ZM .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 1997, 68 (03) :262-274
[10]   Relationship among microstructure, mechanical properties and texture of TA32 titanium alloy sheets during hot tensile deformation [J].
Fan, Rong-lei ;
Wu, Yong ;
Chen, Ming-he ;
Xie, Lan-sheng .
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2020, 30 (04) :928-943