Insights into the carbonization mechanism of bituminous coal-derived carbon materials for lithium-ion and sodium-ion batteries

Despite recent interest in the low-temperature carbonization of coal to prepare disordered carbon materials for the anodes of lithiumion (LIBs) and sodium-ion batteries (SIBs), the carbonization mechanism is still poorly understood. We selected bituminous coal as the raw material and investigated the chemical, microcrystal, and pore structure changes during the carbonization process from coal to the resulting disordered carbon. These structural changes with temperature below 1 000 degrees C show an increase in both interlayer spacing (3.69-3.82 angstrom) and defect concentration (1.26-1.90), accompanied by the generation of a large amount of nano-microporous materials. These changes are attributed to the migration of the local carbon layer and the release of small molecules. Furthermore, a decrease in interlayer spacing and defect concentration occurs between1 000 degrees C and 1 600 degrees C. In LIBs, samples carbonized at 1 000 degrees C showed the best electrochemical performance, with a reversible capacity of 384 mAh g(-1) at 0.1 C and excellent rate performance, maintaining 170 mAh g(-1) at 5 C. In SIBs, samples carbonized at 1 200 degrees C had a reversible capacity of 270.1 mAh g(-1) at 0.1 C and a high initial Coulombic efficiency of 86.8%. This study offers theoretical support for refining the preparation of carbon materials derived from coal.