Microstructure and Mechanical Properties of Hot Pressed Oxide Dispersion Strengthened NITRONIC-60 Austenitic Stainless Steels Developed Through Mechanical Alloying

被引:1
|
作者
Mariappan, R. [1 ]
Chandradass, J. [2 ]
Murali, M. [1 ]
机构
[1] Saranathan Coll Engn, Dept Phys, Trichy 620012, India
[2] SRMIST, Ctr Automot Mat, Dept Automobile Engn, Chengalpattu 603203, India
关键词
Austenitic stainless steel; Oxide dispersion strengthening; Mechanical milling; Micro-structure; Tensile strength; TEMPERATURE;
D O I
10.1007/s13632-023-00928-4
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
In the present study, three different steels were developed from water atomized pre-alloyed powder such as N60 (17Cr-8Mn-4Si), MM-N60 (Mechanical Milled 17Cr-8Mn-4Si) and MM-N60-Y (Mechanical Milled 17Cr-8Mn-4Si-0.3Y(2)O(3)) with and without addition of Yttria. MM-N60 and MM-N60-Y were mechanically milled under high energy ball mill for the period of 2, 4, 6, 8 and 10 h to obtain nanocrystallite structure followed by hot pressing at the temperature of 1250 +/- 10 degrees C with a pressure level of 56 MPa. For comparison, the un-milled powder was also consolidated into a bulk sample under the same processing condition. The microstructure of all three hot-pressed samples was examined under optical, scanning electron, and transmission electron microscopes. Using a Hounsfield tensometer and Vicker's microhardness tester, the mechanical characteristics of these samples were assessed. The grain size of hot pressed samples from the milled powders is lesser than the compact of the un-milled powder. The Y2O3 added austenitic stainless steel (MM-N60-Y) shows the least austenite grains size around 2.8 mu m compared to MM-N60 (without Y2O3). Such a highly refined austenitic grain with Y2O3 dispersoid resulted in the highest hardness, yield, and tensile strength among the three samples. The tensile strength of as high as 758 MPa and a hardness of 484 VHN were obtained in the nano-Y2O3 dispersed ODS austenitic alloy.
引用
收藏
页码:26 / 33
页数:8
相关论文
共 50 条
  • [1] Microstructure and Mechanical Properties of Hot Pressed Oxide Dispersion Strengthened NITRONIC-60 Austenitic Stainless Steels Developed Through Mechanical Alloying
    R. Mariappan
    J. Chandradass
    M. Murali
    Metallography, Microstructure, and Analysis, 2023, 12 : 26 - 33
  • [2] Evolution of microstructure and mechanical properties of an oxide dispersion strengthened austenitic steel during aging at 973 K
    Sun, Shengying
    Zhou, Zhangjian
    Xu, Shuai
    Gao, Yuan
    Wang, Qi
    Wu, Yuchuan
    MATERIALS RESEARCH EXPRESS, 2019, 6 (08)
  • [3] Oxide dispersion strengthened magnesium: Effect of sonicated dispersion on the microstructure and mechanical properties
    Hassan, S. F.
    KOVOVE MATERIALY-METALLIC MATERIALS, 2021, 59 (01): : 1 - 9
  • [4] The Effects of Cold Work on the Microstructure and Mechanical Properties of Intermetallic Strengthened Alumina-Forming Austenitic Stainless Steels
    Hu, B.
    Trotter, G.
    Baker, Ian
    Miller, M. K.
    Yao, L.
    Chen, S.
    Cai, Z.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2015, 46A (08): : 3773 - 3785
  • [5] Microstructure and mechanical properties of austenitic stainless steels manipulated by trace TiC-TiB2 nanoparticles
    Chen, Qianwei
    Wang, Bingxu
    Xu, Yong
    Qiu, Feng
    Dong, Baixin
    Chen, Xiaofu
    Chen, Deli
    Cai, Gaoshen
    Barber, Gary C.
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2024, 33 : 7977 - 7989
  • [6] Microstructure evolution of the oxide dispersion strengthened CLAM steel during mechanical alloying process
    Song, Liangliang
    Liu, Shaojun
    Mao, Xiaodong
    FUSION ENGINEERING AND DESIGN, 2016, 112 : 460 - 467
  • [7] Enhanced Mechanical Properties through Reversion in Metastable Austenitic Stainless Steels
    M.C. Somani
    P. Juntunen
    L.P. Karjalainen
    R.D.K. Misra
    A. Kyröläinen
    Metallurgical and Materials Transactions A, 2009, 40 : 729 - 744
  • [8] Development of Oxide Dispersed Austenitic Stainless Steel through Mechanical Alloying and Spark Plasma Sintering
    Koul, Supriya
    Shivam, Vikas
    Chattopadhyay, Kausik
    Manna, R.
    Biswas, Krishanu
    Mukhopadhyay, N. K.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2022, 31 (11) : 9522 - 9533
  • [9] Welding, mechanical properties and microstructure of different grades of austenitic stainless steels: A review
    Singh, Sahadevuda Sai Rakesh
    Praneeth, Rayala Venkata
    Sankalp, Valluri Sai
    Karthikeyan, R.
    MATERIALS TODAY-PROCEEDINGS, 2022, 62 : 3675 - 3680
  • [10] Microstructure and mechanical properties of common straight carbon steels strengthened by TiC dispersion
    Wu, QianLin
    Sun, Yangshan
    Yang, Caiding
    Xue, Feng
    Song, Fengming
    MATERIALS TRANSACTIONS, 2006, 47 (09) : 2393 - 2398