FATIGUE STRENGTH OF Al-Cu CAST ALLOY WITH DIFFERENT POURING TEMPERATURE

被引：0
|
作者：
Akhyar [1 ]
Iswanto, P. T. [2 ]
Malau, V. [2 ]
Putra, F. P. [2 ]
Farhan, A. [3 ]
机构：
[1] Univ Syiah Kuala, Dept Mech Engn, Jln Syech Abdurrauf 7, Banda Aceh 23111, Indonesia
[2] Gadjah Mada Univ UGM, Dept Mech & Ind Engn, Jln Grafika 2, Yogyakarta 55281, Indonesia
[3] FKIP Univ Syiah Kuala, Dept Phys Educ, Banda Aceh, Indonesia
来源：
METALURGIJA | 2024年 / 63卷 / 02期
关键词：
Al-Cu cast alloy; fatigue strength; tensile strength; pouring temperature; microstructure;
D O I：
暂无
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
This experiment aimed to evaluate how pouring temperature affects fatigue strength of Al-Cu cast alloy. Subsequently, commercial aluminum ingots, such as Al-2024 were remelted and then machined into samples for both tensile and fatigue testing. These samples were cast at three different temperature of 688, 738, and 788 oC while maintaining a constant mold temperature of 220 oC. The results showed that the highest tensile strength was 201,06 MPa at 738 oC. Additionally, the greatest fatigue strength was observed at 80,4 MPa at pouring temperature of 738 oC. It was observed that variations in pouring temperature can significantly impact fatigue strength of cast alloy. At the highest pouring temperature of 788 degrees C, the presence of pores in the metal casting samples resulted in a decrease in both tensile and fatigue strength. Furthermore, when examining the surface fractography of casting sample, the presence of brittle cracks in alloy was observed.
引用
收藏
页码：197 / 200
页数：4
相关论文
共 50 条
  • [1] Nanoparticle additions promote outstanding fracture toughness and fatigue strength in a cast Al-Cu alloy
    Yang, Chenglin
    Zhao, Qinglong
    Zhang, Zhenjun
    Li, Linlin
    Tian, Weisi
    Liu, Rui
    Zhang, Peng
    Xu, Yijiang
    Li, Yanjun
    Zhang, Zhefeng
    Jiang, Qichuan
    Ritchie, Robert O.
    MATERIALS & DESIGN, 2020, 186
  • [2] Characterization of an Al-Cu cast alloy
    Talamantes-Silva, M. A.
    Rodriguez, A.
    Talamantes-Silva, J.
    Valtierra, S.
    Colas, Rafael
    MATERIALS CHARACTERIZATION, 2008, 59 (10) : 1434 - 1439
  • [3] Evolution of microstructure in centrifugal cast Al-Cu alloy
    Sui Yanwei1
    2.School of Materials Science and Engineering
    3.Department of Mechanical Engineering
    China Foundry, 2010, 7 (01) : 43 - 46
  • [4] Evolution of microstructure in centrifugal cast Al-Cu alloy
    Sui Yanwei
    Li Bangsheng
    Liu Aihui
    Guo Jingjie
    Fu Hengzhi
    CHINA FOUNDRY, 2010, 7 (01) : 43 - 46
  • [5] Optimization of Al-Cu Cast Alloy Composition for Hydraulic Valves
    Li, Rong
    Chen, Lunjun
    Zeng, Qi
    Su, Ming
    Xie, Zhiping
    ARCHIVES OF FOUNDRY ENGINEERING, 2020, 20 (01) : 84 - 94
  • [6] Effect of variations in pouring temperature on tensile strength of CuZn cast alloys
    Akhyar
    Iqbal
    Ali, Nurdin
    Husin, Husni
    MATERIALS LETTERS-X, 2023, 17
  • [7] Effect of Soft Surface Layer on Fatigue Strength of Age-Hardened Al-Cu Alloy
    Kanadani, T.
    Nakagawa, K.
    Sakakibara, A.
    Murakami, K.
    Hino, M.
    11TH INTERNATIONAL CONFERENCE ON THE MECHANICAL BEHAVIOR OF MATERIALS (ICM11), 2011, 10
  • [8] Characterization of a Cast Al-Cu Alloy for Automotive Cylinder Head Applications
    Andilab, Bernoulli
    Vandersluis, Eli
    Emadi, Payam
    Ravindran, Comondore
    Byczynski, Glenn
    Fernandez-Gutierrez, Ricardo
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2022, 31 (07) : 5679 - 5688
  • [9] Characterization of a Cast Al-Cu Alloy for Automotive Cylinder Head Applications
    Bernoulli Andilab
    Eli Vandersluis
    Payam Emadi
    Comondore Ravindran
    Glenn Byczynski
    Ricardo Fernández-Gutiérrez
    Journal of Materials Engineering and Performance, 2022, 31 : 5679 - 5688
  • [10] Enhanced mechanical properties of high-temperature-resistant Al-Cu cast alloy by microalloying with Mg
    Rakhmonov, Jovid
    Liu, Kun
    Pan, Lei
    Breton, Francis
    Chen, X-Grant
    JOURNAL OF ALLOYS AND COMPOUNDS, 2020, 827
12345