An influence of nickel with heat treatment on the microstructure and fracture toughness of austempered ductile iron Influence du nickel avec traitement thermique sur la microstructure et la tenacite a la rupture de la fonte ductile a trempe bainitique

被引：0

作者：

Raghavendra, Subramanya ^{[1
]}

Raghavendra, J., V ^{[2
]}

Narayanappa, Manjunatha Kuntanahalli ^{[3
]}

Anjinappa, Chandra Shekar ^{[4
]}

Srinivas, K. G. ^{[4
]}

Manjunatha, B. ^{[5
]}

机构：

[1] Saividya Inst Technol, Dept Mech Engn, Bangalore, Karnataka, India

[2] Jyothy Inst Technol, Dept Mech Engn, Bangalore, Karnataka, India

[3] SJC Inst Technol, Dept Mech Engn, Chikaballpura, India

[4] Bangalore Inst Technol, Dept Mech Engn, Bangalore, Karnataka, India

[5] Acharya Inst Technol, Dept Mech Engn, Bangalore, Karnataka, India

来源：

CANADIAN METALLURGICAL QUARTERLY | 2023年 / 62卷 / 02期

关键词：

Austempered ductile iron; fracture toughness; heat treatment; microsturucture; alloy; nickel; Nodular Iron; Hardness; ADI; BEHAVIOR; ABRASION; WEAR;

D O I：

10.1080/00084433.2022.2088172

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

In this study, unalloyed and nickel alloyed permanent moulded Austempered Ductile Iron (PMADI) samples are utilised to evaluate and compare properties such as tensile hardness and fracture toughness. All PMADI samples were austempered at 350 degrees C for 150 minutes to improve mechanical properties. When compared to unalloyed PMADI samples, PMADI samples alloyed with 1.5% nickel showed better hardness, tensile, and fracture toughness characteristics. In addition to the microstructure examination on samples to determine the presence of feathery dispersion of Bainite, an X-Ray Diffraction Analysis was done to confirm the presence of austenite.