Effect of Temperature on Hard TiB2-Al2O3-Ti Coatings Deposited Using Electron Beam Physical Vapor Deposition

被引：1
作者：
Ali, Ajaz [1 ]
AhmadnAff, Sheikh Nazir [1 ]
机构：
[1] Natl Inst Technol, Dept Mech Engn, Srinagar 190006, Jammu & Kashmir, India
来源：
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE | 2023年 / 32卷 / 10期
关键词：
Al2O3; coatings; nanoindentation; temperature; thin-film; TiB2; tribology; THERMAL BARRIER COATINGS; SUBSTRATE ROTATION; MECHANICAL-PROPERTIES; TEXTURE EVOLUTION; MICROSTRUCTURE; SURFACE; STABILITY; BEHAVIOR; MODULUS; LOAD;
D O I：
10.1007/s11665-022-07414-y
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
High-speed steel surfaces were coated with TiB2-Al2O3-(Ti 20%) thin film coatings of 4.9796 and 3.9036 mu m thickness, deposited using electron beam physical vapor deposition at 400 and 500 degrees C temperatures, respectively. Surface profilometer and 3D profilometer with AFM were used to analyze the coatings' thickness and surface roughness of the samples. Nanotribometer tests were used to evaluate thin film coatings' wear and friction behavior at varied loads of 0.5, 1, 1.5, and 2 N. Nanoindentation, FESEM, EDS, Raman Spectroscopy, and XRD were used to characterize the thin films. According to the findings, the nano-mechanical and nano-tribological behavior of the coating alters at different temperatures. The coating deposition which was done at low temperature of 400 degrees C performed better than the coating deposited high temperature of 500 degrees C.
引用
收藏
页码：4604 / 4625
页数：22
相关论文
共 53 条
[1]   Adapting of sol-gel process for preparation of TiB2 powder from low-cost precursors [J].
Baca, L. ;
Stelzer, N. .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2008, 28 (05) :907-911
[2]   Friction and abrasive wear behaviour of Al2O3-13TiO2 and Al2O3-13TiO2+Ni Graphite coatings [J].
Bagde, Pranay ;
Sapate, S. G. ;
Khatirkar, R. K. ;
Vashishtha, Nitesh .
TRIBOLOGY INTERNATIONAL, 2018, 121 :353-372
[3]   Controlling the B/Ti ratio of TiBx thin films grown by high-power impulse magnetron sputtering [J].
Bakhit, Babak ;
Petrov, Ivan ;
Greene, J. E. ;
Hultman, Lars ;
Rosen, Johanna ;
Greczynski, Grzegorz .
JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A, 2018, 36 (03)
[4]   Nanomechanical and nanotribological characterization of multilayer self-lubricating Ti/MoS2/Si/MoS2 nanocoating on aluminium-silicon substrate [J].
Banday, Summera ;
Wani, M. F. .
SURFACE AND INTERFACE ANALYSIS, 2019, 51 (06) :649-660
[5]   Evaluation of magnetron-sputtered TiB2 intended for tribological applications [J].
Berger, M ;
Larsson, M ;
Hogmark, S .
SURFACE & COATINGS TECHNOLOGY, 2000, 124 (2-3) :253-261
[6]   High-performance coatings for cutting tools [J].
Bobzin, Kirsten .
CIRP JOURNAL OF MANUFACTURING SCIENCE AND TECHNOLOGY, 2017, 18 :1-9
[7]   Morphological analysis of TiB2 thin film prepared by rf magnetron sputtering [J].
Dai, Wei ;
Zhang, Tongjun ;
Yang, Junyou ;
Sun, Rongxing ;
Xu, Juliang .
JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A, 2008, 26 (04) :610-615
[8]   Synthesis of α-Al2O3-graphene composite: a novel product to provide multi-functionalities on steel strip surface [J].
Dash, Tapan ;
Rout, Tapan Kumar ;
Palei, Binod Bihari ;
Bajpai, Shubhra ;
Kundu, Saurabh ;
Bhagat, Amar N. ;
Satpathy, Bijoy Kumar ;
Biswal, Susanta Kumar ;
Rajput, Abhinay ;
Sahu, Ashok Kumar ;
Biswal, Surendra Kumar .
SN APPLIED SCIENCES, 2020, 2 (07)
[9]   Visible light absorption of surface-modified Al2O3 powders: A comparative DFT and experimental study [J].
Dordevic, Vesna ;
Sredojevic, Dusan N. ;
Dostanic, Jasmina ;
Loncarevic, Davor ;
Ahrenkiel, S. Phillip ;
Svrakic, Nenad ;
Brothers, Edward ;
Belic, Milivoj ;
Nedeljkovic, Jovan M. .
MICROPOROUS AND MESOPOROUS MATERIALS, 2019, 273 :41-49
[10]   Synthesis of TiB2-TiC/Fe nano-composite coating by laser surface engineering [J].
Du, Baoshuai ;
Paital, Sameer R. ;
Dahotre, Narendra B. .
OPTICS AND LASER TECHNOLOGY, 2013, 45 :647-653
123456