Microstructural stability and high temperature strength of directionally solidified Al2O3/Er3Al5O12/ZrO2 eutectic ceramics

被引:2
作者
Wang, Shunheng [1 ,2 ,3 ]
Liu, Juncheng [1 ]
Lan, Dehui [1 ]
Gao, Rui [1 ]
Torre, Jose Ignacio Pena [3 ]
机构
[1] Tiangong Univ, Sch Mat Sci & Engn, Tianjin 300387, Peoples R China
[2] Binzhou Inst Technol, Weiqiao UCAS Sci & Technol Pk, Binzhou 256606, Shandong, Peoples R China
[3] Univ Zaragoza, CSIC, Inst Ciencia Mat Aragon, Zaragoza 50018, Spain
关键词
Coarsening; Heat treatment; High temperature strength; Directional solidification; MECHANICAL-PROPERTIES; SURFACE-DIFFUSION; GROWTH; COMPOSITE; PHASE;
D O I
10.1016/j.ceramint.2023.10.104
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Al2O3/Er3Al5O12(EAG)/ZrO2 directionally solidified eutectic ceramics (DSECs) were prepared with high frequency induction heating zone melting (IHZM), and heat treated at high temperature. Their phase components, microstructures, flexural and tensile strengths were investigated. The results indicated that the microstructures were composed of the mutually interpenetrated Al2O3, EAG and ZrO2 (stabilized by Er3+ ion) phases. As the growth rate increased from 2 mm/h to 20 mm/h, the phase size decreased and the irregular microstructure became regular. When the heat treatment temperature was up to 1400 degrees C, the ionic diffusion was triggered and the phase began to grow. Under the action of surface energy and special microstructure, the growth of phase stopped after it reached a certain threshold. The sample with smaller phase size exhibited higher strength at room temperature, which was dependent on the crack propagation resistance. However, the speed of strength reduction was faster. The formation of surface groove, microcrack and malignant growth phase was responsible for this rapidly decreasing of strength. The flexural and tensile strengths of eutectic ceramic with larger phase size remained at 671.6 MPa and 359.45 MPa after long-term heat treatment at 1500 degrees C, respectively. The smaller difference between the original phase size and the maximum coarsened phase size was beneficial to avoid the occurrence of the above mentioned harmful factors and was the source of strength stability.
引用
收藏
页码:306 / 314
页数:9
相关论文
共 43 条
[1]  
Abal S., 2017, High Temp. Mater. Process., V36, P1
[2]  
Akira Y., 1999, Jpn. J. Appl. Phys., V38, P55
[3]   Effect of moisture on the high-temperature stability of unidirectionally solidified Al2O3/YAG eutectic composites [J].
Bahlawane, N ;
Watanabe, T ;
Waku, Y ;
Mitani, A ;
Nakagawa, N .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2000, 83 (12) :3077-3081
[4]   Tensile strength and microstructure of Al2O3-ZrO2 hypo-eutectic fibers [J].
Farmer, SC ;
Sayir, A .
ENGINEERING FRACTURE MECHANICS, 2002, 69 (09) :1015-1024
[5]   High temperature creep deformation of directionally solidified Al2O3/Er3Al5O12 [J].
Fernandez, JM ;
Sayir, A ;
Farmer, SC .
ACTA MATERIALIA, 2003, 51 (06) :1705-1720
[6]   High temperature mechanical retention characteristics and oxidation behaviors of the MoSi2(Cr5Si3)RSiC composites prepared via a PIPAAMI combined process [J].
Gao, Peng-zhao ;
Cheng, Lei ;
Yuan, Zheng ;
Liu, Xiao-pan ;
Xiao, Han-ning .
JOURNAL OF ADVANCED CERAMICS, 2019, 8 (02) :196-208
[7]   NEW METHOD OF OBTAINING VOLUME GRAIN-BOUNDARY AND SURFACE DIFFUSION COEFFICIENTS FROM SINTERING DATA [J].
JOHNSON, DL .
JOURNAL OF APPLIED PHYSICS, 1969, 40 (01) :192-&
[8]   Phase diagram of the Al2O3-ZrO2-Er2O3 system.: III.: Solidus surface and phase equilibria in alloy crystallization [J].
Lakiza, S. M. ;
Red'ko, V. P. ;
Lopato, L. M. .
POWDER METALLURGY AND METAL CERAMICS, 2007, 46 (5-6) :266-273
[9]   Microstructure of Y2O3 doped Al2O3/ZrO2 eutectic fibers grown by the micro-pulling-down method [J].
Lee, JH ;
Yoshikawa, A ;
Kaiden, H ;
Lebbou, K ;
Fukuda, T ;
Yoon, DH ;
Waku, Y .
JOURNAL OF CRYSTAL GROWTH, 2001, 231 (1-2) :179-185
[10]   Microstructure of Al2O3/ZrO2 eutectic fibers grown by the micro-pulling down method [J].
Lee, JH ;
Yoshikawa, A ;
Durbin, SD ;
Yoon, DH ;
Fukuda, T ;
Waku, Y .
JOURNAL OF CRYSTAL GROWTH, 2001, 222 (04) :791-796