Effect of varying carbon microstructures on the ion storage behavior of dual carbon lithium-ion capacitor

Dual carbon lithium-ion capacitors (LICs) are the next-generation hybrid energy storage devices that aim towards energy-power balanced applications. Thus, tuning the properties of the carbon electrode materials is a crucial step toward optimizing the device's performance. Herein, the effect of change in the microstructure of the carbon electrodes on the ion storage capacity and their consequent energy-power manifestation is investigated. The optimized carbonaceous anode calcined at 700 degrees C delivers 290 mAh g(-1) capacity after 1000 cycles at 1 A g(-1). This superiority in performance is attributed to the formation of micron-size channels and mesopores for better ion transport and storage. In contrast, the activated carbon cathode delivers a capacitance of 118 F g(-1) and retains 76% at the end of 5000 cycles. The LIC full cell with these electrode materials provides maximum energy of 120 Wh kg(-1), a maximum power density of 20.7 kW kg(-1) and cycles till 9000 cycles with similar to 67% capacitance retention. The mechanistic control over the deliverable ion storage capacity is also analyzed for the LIC full cell. Furthermore, the lighting demonstration, self-discharge studies, leakage current, and electrochemical impedance are recorded to elucidate the practical feasibility and performance degradation mechanism of the coin-cell device.