ESR Modeling for Atmospheric Corrosion Behavior of Metallized Film Capacitors

被引：3
|
作者：
Li, Hua [1 ]
Qiu, Tian [1 ]
Li, Zheng [1 ]
Lin, Fuchang [1 ]
Wang, Yan [1 ]
机构：
[1] Huazhong Univ Sci & Technol, Sch Elect & Elect Engn, State Key Lab Adv Electromagnet Engn & Technol, Wuhan 430074, Peoples R China
来源：
IEEE TRANSACTIONS ON DEVICE AND MATERIALS RELIABILITY | 2023年 / 23卷 / 04期
基金：
中国国家自然科学基金;
关键词：
Metallized film capacitors; atmospheric corrosion; ESR modeling; metal composition; end contact; PERFORMANCE; TECHNOLOGY; OXIDATION; ALUMINUM;
D O I：
10.1109/TDMR.2023.3309914
中图分类号：
TM [电工技术]; TN [电子技术、通信技术];
学科分类号：
0808 ; 0809 ;
摘要：
Atmospheric corrosion significantly affects the reliability of metallized film capacitors (MFCs). Oxygen and moisture will induce oxidation reactions that lead to electrode corrosion, elevating the equivalent series resistance (ESR). In this work, an ESR elevation model is proposed to study the mechanism and regularity of the corrosion, and the influence of metal composition is analyzed with the accelerated aging test. It is found that the anti-corrosion ability results from the oxide structure on electrodes, with a transition from oxide plates to a compact oxide film as Al content ascends. The end contact degradation of MFCs has a notable impact on the ESR elevation, which can be inhibited by increasing the Al content to over 50 wt.%.
引用
收藏
页码：486 / 493
页数：8
相关论文
共 50 条
  • [41] Effects of Electromagnetic Field on Partial Discharge Behavior in BOPP Film Capacitors
    Liu, Haoliang
    Du, Boxue
    Xiao, Meng
    Ma, Yanwei
    IEEE TRANSACTIONS ON DIELECTRICS AND ELECTRICAL INSULATION, 2023, 30 (06) : 2617 - 2624
  • [42] Artificial neural network modeling of atmospheric corrosion in the MICAT project
    Pintos, S
    Queipo, NV
    de Rincón, OT
    Rincón, A
    Morcillo, R
    CORROSION SCIENCE, 2000, 42 (01) : 35 - 52
  • [43] Corrosion behavior on aluminum alloy LY12 in simulated atmospheric corrosion process
    王振尧
    马腾
    韩薇
    于国才
    Transactions of Nonferrous Metals Society of China, 2007, (02) : 326 - 334
  • [44] Corrosion behavior on aluminum alloy LY12 in simulated atmospheric corrosion process
    Wang Zhen-yao
    Ma Teng
    Han Wei
    Yu Guo-cai
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2007, 17 (02) : 326 - 334
  • [45] Atmospheric corrosion monitoring of a weathering steel under an electrolyte film in cyclic wet-dry condition
    Thee, Ch.
    Hao, Long
    Dong, Junhua
    Mu, Xin
    Wei, Xin
    Li, Xiaofang
    Ke, Wei
    CORROSION SCIENCE, 2014, 78 : 130 - 137
  • [46] Atmospheric Corrosion Behavior of Weathering Steel in Periodically Changed Environment
    Zhang, Xu
    Yang, Shanwu
    Guo, Hui
    He, Xinlai
    ISIJ INTERNATIONAL, 2014, 54 (04) : 909 - 915
  • [47] Long-Term Atmospheric Corrosion Behavior of Epoxy Prime Coated Aluminum Alloy 7075-T6 in Coastal Environment
    Zhang, Sheng
    He, Yuting
    Zhang, Teng
    Wang, Guirong
    Du, Xu
    MATERIALS, 2018, 11 (06):
  • [48] Atmospheric Corrosion Behavior of Salvaged Marine Cast Iron Artifacts
    Ouyang, Weizhen
    MATERIAL DESIGN, PROCESSING AND APPLICATIONS, PARTS 1-4, 2013, 690-693 : 97 - 100
  • [49] Hydrogen Entry Behavior into Iron and Steel under Atmospheric Corrosion
    Li, Songjie
    Akiyama, Eiji
    Shinohara, Tadashi
    Matsuoka, Kazumi
    Oshikawa, Wataru
    ISIJ INTERNATIONAL, 2013, 53 (06) : 1062 - 1069
  • [50] Hydrogen Entry Behavior into Iron and Steels under Atmospheric Corrosion
    Li, Songjie
    Akiyama, Eiji
    Shinohara, Tadashi
    Matsuoka, Kazumi
    Oshikawa, Wataru
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 2013, 99 (11): : 651 - 658
12345