Performance Comparison of SONOS-Type UV TD Sensor Using Indium Tin Oxide-Aluminum Oxide-Zirconia Aluminum Oxide-Silicon Oxide-Silicon and Indium Tin Oxide-Aluminum Oxide-Hafnium Aluminum Oxide-Silicon Oxide-Silicon

This study compares the performance of two types of capacitive devices, indium tin oxide-aluminum oxide-zirconia aluminum oxide-silicon oxide-silicon (IAZAOS) and indium tin oxide-aluminum oxide-hafnium aluminum oxide-silicon oxide-silicon (IAHAOS), as silicon-oxide-nitride-oxide-silicon (SONOS) non-volatile memory (NVM) total dose of ultraviolet radiation (UV TD) sensors. Results show that IAZAOS with zirconia aluminum oxide as the charge-trapping layer outperforms IAHAOS with hafnium aluminum oxide for a UV TD sensor. After exposure to UV TD irradiation of 100 mW & BULL;s/cm(2), the threshold voltage (V-T) change of IAZAOS is almost 1.25 times that of IAHAOS. The study also found that annealing can significantly improve the response performance of IAZAOS UV TD sensors. Furthermore, IAZAOS devices with partially smaller nanocrystals in the charge-trapping layer greatly enhance the response of SONOS-type UV TD sensors. The study also compared the constant voltage stress-induced leakage current (CVSILC) and found that the CVSILC for annealed IAZAOS devices is 1000 times smaller than that of IAHAOS devices. Moreover, the IAZAOS-I2Z2 exhibits a superior performance regarding irradiation/refresh cycle endurance as compared to the IAHAOS-I2H1 device. These findings suggest that IAZAOS capacitive devices have superior performance and potential for use in SONOS-type UV TD sensors.