Failure mechanism and life correlation of Inconel 718 in high and very high cycle fatigue regimes

被引：11
|
作者：
Yang, Yi-Fan [1 ]
Hu, Hua-Yan [2 ]
Min, Lin [1 ]
Sun, Qian-Tao [1 ]
Song, Miao [2 ]
Zhu, Ming-Liang [1 ]
Wen, Jian-Feng [1 ,3 ]
Tu, Shan-Tung [1 ,3 ]
机构：
[1] East China Univ Sci & Technol, Sch Mech & Power Engn, Key Lab Pressure Syst & Safety, Minist Educ, Shanghai 200237, Peoples R China
[2] Shanghai Jiao Tong Univ, Sch Nucl Sci & Engn, Shanghai 200240, Peoples R China
[3] Shanghai Inst Aircraft Mech & Control, Shanghai 200092, Peoples R China
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2023年 / 175卷
基金：
中国国家自然科学基金;
关键词：
Inconel; 718; Very high cycle fatigue; Fatigue crack initiation; Transmission electron microscopy; Fatigue life; NICKEL-BASED SUPERALLOY; SUBSURFACE CRACK INITIATION; HIGH-STRENGTH STEELS; DISLOCATION CHANNEL; GRAIN-SIZE; ALLOY; BEHAVIOR; MICROSTRUCTURE; INCLUSION; FRACTURE;
D O I：
10.1016/j.ijfatigue.2023.107764
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
High and very high cycle fatigue (HCF and VHCF) behaviours and failure mechanism of Inconel 718 were investigated via ultrasonic fatigue tests and microscopic characterization techniques. It is shown that the S-N curve continuously decreases in the HCF regime, while forming a plateau for VHCF. Cracks initiate from a single site on the surface or subsurface. Site-specific focused ion beam sampling and transmission electron microscopy characterization reveal that the crack initiation is governed by slip-induced localized plastic deformation. Microcracks initiate near non-metallic inclusions or slip band-grain boundary site. Plus, a life correlation model considering the size of micro-defect was proposed to better correlate the fatigue life.
引用
收藏
页数：13
相关论文
共 50 条
  • [31] High-cycle fatigue properties at cryogenic temperatures in INCONEL 718 nickel-based superalloy
    Ono, Y
    Yuri, T
    Sumiyoshi, H
    Takeuchi, E
    Matsuoka, S
    Ogata, T
    MATERIALS TRANSACTIONS, 2004, 45 (02) : 342 - 345
  • [32] The influence of Laves phases on the high-cycle fatigue behavior of laser additive manufactured Inconel 718
    Sui, Shang
    Chen, Jing
    Fan, Enxiang
    Yang, Haiou
    Lin, Xin
    Huang, Weidong
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2017, 695 : 6 - 13
  • [33] Very high cycle fatigue of surface carburized CrNi steel at variable stress ratio: Failure analysis and life prediction
    Nehila, Abdelhak
    Li, Wei
    Gao, Ning
    Xing, Xinxin
    Zhao, Hongqiao
    Wang, Ping
    Sakai, Tatsuo
    INTERNATIONAL JOURNAL OF FATIGUE, 2018, 111 : 112 - 123
  • [34] Effects of intermittent loading on fatigue life of a high strength steel in very high cycle fatigue regime
    Sun, Chengqi
    Song, Qingyuan
    Hu, Yuanpei
    Wei, Yujie
    INTERNATIONAL JOURNAL OF FATIGUE, 2018, 117 : 9 - 12
  • [35] Correlation between Surface Integrity and Low Cycle Fatigue Life of Machined Inconel 718
    Cui, Pengcheng
    Liu, Zhanqiang
    Zhao, Jinfu
    Ren, Xiaoping
    METALS, 2024, 14 (02)
  • [36] Mechanism of subsurface microstructural fatigue crack initiation during high and very-high cycle fatigue of advanced bainitic steels
    Gao, Guhui
    Liu, Rong
    Fan, Yusong
    Qian, Guian
    Gui, Xiaolu
    Misra, R. D. K.
    Bai, Bingzhe
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2022, 108 : 142 - 157
  • [37] Effects of sandblasting and HIP on very high cycle fatigue performance of SLM-fabricated IN718 superalloy
    Yu, Chuanli
    Huang, Zhiyong
    Zhang, Zian
    Wang, Jian
    Shen, Jiebin
    Xu, Zhiping
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2022, 18 : 29 - 43
  • [38] Very high cycle fatigue of TC4 titanium alloy under variable stress ratio: Failure mechanism and life prediction
    Li, Wei
    Zhao, Hongqiao
    Nehila, Abdelhak
    Zhang, Zhenyu
    Sakai, Tatsuo
    INTERNATIONAL JOURNAL OF FATIGUE, 2017, 104 : 342 - 354
  • [39] Influence of turning parameters on the high-temperature fatigue performance of Inconel 718 superalloy
    Galatolo, R.
    Fanteria, D.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2017, 40 (12) : 2019 - 2031
  • [40] Very high cycle fatigue of bearing steels with artificial defects in vacuum
    Spriestersbach, D.
    Brodyanski, A.
    Loesch, J.
    Kopnarski, M.
    Kerscher, E.
    MATERIALS SCIENCE AND TECHNOLOGY, 2016, 32 (11) : 1111 - 1118
12345