Failure mechanism and life correlation of Inconel 718 in high and very high cycle fatigue regimes

被引：11
|
作者：
Yang, Yi-Fan [1 ]
Hu, Hua-Yan [2 ]
Min, Lin [1 ]
Sun, Qian-Tao [1 ]
Song, Miao [2 ]
Zhu, Ming-Liang [1 ]
Wen, Jian-Feng [1 ,3 ]
Tu, Shan-Tung [1 ,3 ]
机构：
[1] East China Univ Sci & Technol, Sch Mech & Power Engn, Key Lab Pressure Syst & Safety, Minist Educ, Shanghai 200237, Peoples R China
[2] Shanghai Jiao Tong Univ, Sch Nucl Sci & Engn, Shanghai 200240, Peoples R China
[3] Shanghai Inst Aircraft Mech & Control, Shanghai 200092, Peoples R China
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2023年 / 175卷
基金：
中国国家自然科学基金;
关键词：
Inconel; 718; Very high cycle fatigue; Fatigue crack initiation; Transmission electron microscopy; Fatigue life; NICKEL-BASED SUPERALLOY; SUBSURFACE CRACK INITIATION; HIGH-STRENGTH STEELS; DISLOCATION CHANNEL; GRAIN-SIZE; ALLOY; BEHAVIOR; MICROSTRUCTURE; INCLUSION; FRACTURE;
D O I：
10.1016/j.ijfatigue.2023.107764
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
High and very high cycle fatigue (HCF and VHCF) behaviours and failure mechanism of Inconel 718 were investigated via ultrasonic fatigue tests and microscopic characterization techniques. It is shown that the S-N curve continuously decreases in the HCF regime, while forming a plateau for VHCF. Cracks initiate from a single site on the surface or subsurface. Site-specific focused ion beam sampling and transmission electron microscopy characterization reveal that the crack initiation is governed by slip-induced localized plastic deformation. Microcracks initiate near non-metallic inclusions or slip band-grain boundary site. Plus, a life correlation model considering the size of micro-defect was proposed to better correlate the fatigue life.
引用
收藏
页数：13
相关论文
共 50 条
  • [21] Fatigue and fracture behavior of nickel-based superalloy Inconel 718 up to the very high cycle regime
    Xian-feng Ma
    Zheng Duan
    Hui-ji Shi
    Ryosuke Murai
    Eiichi Yanagisawa
    Journal of Zhejiang University-SCIENCE A, 2010, 11 : 727 - 737
  • [22] Fatigue and fracture behavior of nickel-based superalloy Inconel 718 up to the very high cycle regime
    Ryosuke MURAI
    Eiichi YANAGISAWA
    Journal of Zhejiang University-Science A(Applied Physics & Engineering), 2010, 11 (10) : 727 - 737
  • [23] Competing crack initiation behaviors of a laser additively manufactured nickel-based superalloy in high and very high cycle fatigue regimes
    Yang, Kun
    Huang, Qi
    Wang, Qingyuan
    Chen, Qiang
    INTERNATIONAL JOURNAL OF FATIGUE, 2020, 136
  • [24] Effects of electrochemical machining on high-cycle fatigue of Inconel 718 blades
    Ren, Mingzhu
    Zhu, Dong
    Zhou, Xinqun
    Wang, Yunmiao
    ENGINEERING FAILURE ANALYSIS, 2024, 165
  • [25] Crack initiation sensitivity of wrought direct aged alloy 718 in the very high cycle fatigue regime: the role of non-metallic inclusions
    Texier, Damien
    Cormier, Jonathan
    Villechaise, Patrick
    Stinville, Jean-Charles
    Torbet, Chris J.
    Pierret, Stephane
    Pollock, Tresa M.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 678 : 122 - 136
  • [26] Fracture mechanism of Ti60 alloy at high temperature in very high cycle fatigue regime and fatigue life prediction
    Zhou, Qikai
    Huang, Zhiyong
    Qian, Hongjiang
    Wang, Jian
    Shen, Zeshuai
    Pan, Kai
    Chen, Yonghui
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2024, 47 (09) : 3285 - 3299
  • [27] A data-physics integrated approach to life prediction in very high cycle fatigue regime
    Fan, Jia-Le
    Zhu, Gang
    Zhu, Ming-Liang
    Xuan, Fu-Zhen
    INTERNATIONAL JOURNAL OF FATIGUE, 2023, 176
  • [28] Life Prediction Models in very High Cycle Fatigue Regime
    Song Yanan
    Xu Binshi
    Wang Haidou
    Zhang Yubo
    Xing Zhiguo
    RARE METAL MATERIALS AND ENGINEERING, 2016, 45 (05) : 1203 - 1208
  • [29] Interior failure mechanism and life prediction of surface-treated 17Cr-Ni steel under high and very high cycle fatigue
    Nehila, A.
    Li, W.
    Zhao, H.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2018, 41 (06) : 1318 - 1329
  • [30] Mechanism of crack initiation and early growth of high strength steels in very high cycle fatigue regime
    Song, Qingyuan
    Sun, Chengqi
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2020, 771
12345