Failure mechanism and life correlation of Inconel 718 in high and very high cycle fatigue regimes

被引：11
|
作者：
Yang, Yi-Fan [1 ]
Hu, Hua-Yan [2 ]
Min, Lin [1 ]
Sun, Qian-Tao [1 ]
Song, Miao [2 ]
Zhu, Ming-Liang [1 ]
Wen, Jian-Feng [1 ,3 ]
Tu, Shan-Tung [1 ,3 ]
机构：
[1] East China Univ Sci & Technol, Sch Mech & Power Engn, Key Lab Pressure Syst & Safety, Minist Educ, Shanghai 200237, Peoples R China
[2] Shanghai Jiao Tong Univ, Sch Nucl Sci & Engn, Shanghai 200240, Peoples R China
[3] Shanghai Inst Aircraft Mech & Control, Shanghai 200092, Peoples R China
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2023年 / 175卷
基金：
中国国家自然科学基金;
关键词：
Inconel; 718; Very high cycle fatigue; Fatigue crack initiation; Transmission electron microscopy; Fatigue life; NICKEL-BASED SUPERALLOY; SUBSURFACE CRACK INITIATION; HIGH-STRENGTH STEELS; DISLOCATION CHANNEL; GRAIN-SIZE; ALLOY; BEHAVIOR; MICROSTRUCTURE; INCLUSION; FRACTURE;
D O I：
10.1016/j.ijfatigue.2023.107764
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
High and very high cycle fatigue (HCF and VHCF) behaviours and failure mechanism of Inconel 718 were investigated via ultrasonic fatigue tests and microscopic characterization techniques. It is shown that the S-N curve continuously decreases in the HCF regime, while forming a plateau for VHCF. Cracks initiate from a single site on the surface or subsurface. Site-specific focused ion beam sampling and transmission electron microscopy characterization reveal that the crack initiation is governed by slip-induced localized plastic deformation. Microcracks initiate near non-metallic inclusions or slip band-grain boundary site. Plus, a life correlation model considering the size of micro-defect was proposed to better correlate the fatigue life.
引用
收藏
页数：13
相关论文
共 50 条
  • [1] An investigation into the effects of cyclic strain rate on the high cycle and very high cycle fatigue behaviors of wrought and additively manufactured Inconel 718
    Muhammad, Muztahid
    Frye, Palmer
    Simsiriwong, Jutima
    Shao, Shuai
    Shamsaei, Nima
    INTERNATIONAL JOURNAL OF FATIGUE, 2021, 144
  • [2] Very High Cycle Fatigue Investigations on the Fatigue Strength of Additive Manufactured and Conventionally Wrought Inconel 718 at 873 K
    Schmiedel, Alexander
    Burkhardt, Christina
    Henkel, Sebastian
    Weidner, Anja
    Biermann, Horst
    METALS, 2021, 11 (11)
  • [3] Fatigue life and mechanistic modeling of interior micro-defect induced cracking in high cycle and very high cycle regimes
    Zhu, Ming-Liang
    Jin, Long
    Xuan, Fu-Zhen
    ACTA MATERIALIA, 2018, 157 : 259 - 275
  • [4] Effects of specimen size on fatigue life of metallic materials in high-cycle and very-high-cycle fatigue regimes
    Sun, C.
    Zhang, X.
    Liu, X.
    Hong, Y.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2016, 39 (06) : 770 - 779
  • [5] High-cycle fatigue properties at cryogenic temperatures in INCONEL 718
    Ono, Y.
    Yuri, T.
    Sumiyoshi, H.
    Takeuchi, E.
    Matsuoka, S.
    Ogata, T.
    ADVANCES IN CRYOGENIC ENGINEERING, VOL 52A & 52B, 2006, 824 : 184 - +
  • [6] The high-cycle fatigue properties of selective laser melted Inconel 718 at room and elevated temperatures
    Li, W. B.
    Pang, J. C.
    Zhang, H.
    Li, S. X.
    Zhang, Z. F.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2022, 836
  • [7] High cycle and very high cycle fatigue behavior of additively manufactured Inconel 718: Effects of stress-relieving, surface texture, part orientation, and test frequency
    Muhammad, Muztahid
    Lee, Seungjong
    Frye, Palmer
    Simsiriwong, Jutima
    Shao, Shuai
    Shamsaei, Nima
    ENGINEERING FAILURE ANALYSIS, 2025, 169
  • [8] A fatigue life prediction approach to surface and interior inclusion induced high cycle and very-high cycle fatigue for bainite/martensite multiphase steel
    Fan, Yusong
    Gao, Guhui
    Xu, Xiang
    Liu, Rong
    Zhang, Fengming
    Gui, Xiaolu
    INTERNATIONAL JOURNAL OF FATIGUE, 2025, 192
  • [9] Fatigue and fracture behavior of nickel-based superalloy Inconel 718 up to the very high cycle regime
    Ma, Xian-feng
    Duan, Zheng
    Shi, Hui-ji
    Murai, Ryosuke
    Yanagisawa, Eiichi
    JOURNAL OF ZHEJIANG UNIVERSITY-SCIENCE A, 2010, 11 (10): : 727 - 737
  • [10] A cumulative damage model for fatigue life estimation of high-strength steels in high-cycle and very-high-cycle fatigue regimes
    Sun, C.
    Xie, J.
    Zhao, A.
    Lei, Z.
    Hong, Y.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2012, 35 (07) : 638 - 647
12345