Properties of Potassium Doped and Tantalum Containing Tungsten after Heavy Ion Irradiation

被引：0
作者：
Du, Juan [1 ]
Wu, Chuan [1 ,2 ]
Zhao, Tianyu [1 ,2 ]
Wen, Pan [1 ]
Wang, Pinghuai [1 ]
Tang, Jun [2 ]
Liu, Xiang [1 ]
Chen, Jiming [1 ]
机构：
[1] Southwestern Inst Phys, Fus Sci Ctr, Chengdu 610225, Peoples R China
[2] Sichuan Univ, Inst Nucl Sci & Technol, Key Lab Radiat Phys & Technol, Minist Educ, Chengdu, Peoples R China
来源：
CRYSTALS | 2023年 / 13卷 / 06期
基金：
中国国家自然科学基金;
关键词：
tungsten; potassium doped; tantalum alloy; irradiation; hardness; PLASMA; RESISTANCE; ALLOYS; DESIGN;
D O I：
10.3390/cryst13060951
中图分类号：
O7 [晶体学];
学科分类号：
0702 ; 070205 ; 0703 ; 080501 ;
摘要：
Tungsten potassium (WK) alloy has been reported as one of the ideal plasma-facing materials (PFMs). Tantalum alloying is a good method to improve the mechanical properties of tungsten. The effect of tantalum contents on the irradiation resistance of WK alloy has not yet been reported. In this study, WK (containing 82 ppm potassium) alloy with 1 wt. % Ta and 3 wt. % Ta, specifically WK-1Ta and WK-3Ta, were fabricated with sparking plasma sintering and irradiated with 7.5 MeV W2+ ion. The relative densities of WK-1Ta and WK-3Ta are 97.2% and 96.4%, respectively. The average grain sizes of WK-1Ta and WK-3Ta are 2.08 & mu;m and 1.51 & mu;m, respectively. The Vickers hardness of WK-3Ta is nearly 20% higher than that of WK-1Ta, both before and after irradiation. Irradiation hardening was confirmed by nano indentation test results. After irradiation, the number of dislocation loops formed in WK-1Ta and WK-3Ta are very similar, and the dislocation loop density of WK-3Ta is only slightly higher than that of WK-1Ta. This phenomenon is consistent with nano hardness analysis results. Compared to the reported nano hardness results of WK alloys, both WK-1Ta and WK-3Ta had higher hardness than the WK alloys before irradiation. Compared to the irradiation hardening results for the reported WK alloys, the existence of Ta may have positive influence on resistance to irradiation hardening.
引用
收藏
页数：12
相关论文
共 29 条
  • [11] Development of advanced high heat flux and plasma-facing materials
    Linsmeier, Ch.
    Rieth, M.
    Aktaa, J.
    Chikada, T.
    Hoffmann, A.
    Hoffmann, J.
    Houben, A.
    Kurishita, H.
    Jin, X.
    Li, M.
    Litnovsky, A.
    Matsuo, S.
    von Mueller, A.
    Nikolic, V.
    Palacios, T.
    Pippan, R.
    Qu, D.
    Reiser, J.
    Riesch, J.
    Shikama, T.
    Stieglitz, R.
    Weber, T.
    Wurster, S.
    You, J. -H.
    Zhou, Z.
    [J]. NUCLEAR FUSION, 2017, 57 (09)
  • [12] Irradiation effects of hydrogen and helium plasma on different grade tungsten materials
    Liu, X.
    Lian, Y. Y.
    Greuner, H.
    Boeswirth, B.
    Jin, Y. Z.
    Feng, F.
    Wang, J. B.
    Chen, L.
    Song, J. P.
    Yu, Y.
    Zhang, T.
    Liu, C. S.
    Tan, J.
    Liu, D. P.
    Duan, X. R.
    [J]. NUCLEAR MATERIALS AND ENERGY, 2017, 12 : 1314 - 1318
  • [13] Surface modification and deuterium retention in hot-rolled potassium doped tungsten alloy exposed to deuterium plasma
    Ma, Xiaolei
    Wang, Ting
    Zhang, Xiaoxin
    Yuan, Yue
    Cheng, Long
    Zhu, Jipeng
    Lv, Wei
    Lang, Shaoting
    Wang, Zihao
    Ge, Changchun
    Yan, Qingzhi
    [J]. JOURNAL OF NUCLEAR MATERIALS, 2022, 568
  • [14] Large-scale potassium-doped tungsten alloy with superior recrystallization resistance, ductility and strength induced by potassium bubbles
    Ma, Xiaolei
    Zhang, Xiaoxin
    Wang, Ting
    Lang, Shaoting
    Lv, Wei
    Wang, Yijia
    Ge, Changchun
    Yan, Qingzhi
    [J]. JOURNAL OF NUCLEAR MATERIALS, 2022, 559
  • [15] Irradiation hardening behaviors of large-scale hot rolling potassium-doped tungsten alloy under synergistic irradiations of Fe11+ ion combined with deuterium and helium plasmas
    Ma, Xiaolei
    Zhang, Xiaoxin
    Wang, Ting
    Lv, Wei
    Lang, Shaoting
    Ge, Changchun
    Yan, Qingzhi
    [J]. NUCLEAR MATERIALS AND ENERGY, 2022, 30
  • [16] Neutron irradiation tolerance of potassium-doped and rhenium-alloyed tungsten
    Nogami, Shuhei
    Terentyev, Dmitry
    Zinovev, Aleksandr
    Yin, Chao
    Rieth, Michael
    Pintsuk, Gerald
    Hasegawa, Akira
    [J]. JOURNAL OF NUCLEAR MATERIALS, 2021, 553
  • [17] Recent analysis of key plasma wall interactions issues for ITER
    Roth, Joachim
    Tsitrone, E.
    Loarte, A.
    Loarer, Th.
    Counsell, G.
    Neu, R.
    Philipps, V.
    Brezinsek, S.
    Lehnen, M.
    Coad, P.
    Grisolia, Ch.
    Schmid, K.
    Krieger, K.
    Kallenbach, A.
    Lipschultz, B.
    Doerner, R.
    Causey, R.
    Alimov, V.
    Shu, W.
    Ogorodnikova, O.
    Kirschner, A.
    Federici, G.
    Kukushkin, A.
    [J]. JOURNAL OF NUCLEAR MATERIALS, 2009, 390-91 : 1 - 9
  • [18] Hardening effect of multi-energyW2+-ion irradiation on tungsten-potassium alloy*
    Song, Yang-Yi-Peng
    Qiu, Wen-Bin
    Chen, Long-Qing
    Yang, Xiao-Liang
    Deng, Hao
    Liu, Chang-Song
    Zhang, Kun
    Tang, Jun
    [J]. CHINESE PHYSICS B, 2020, 29 (10)
  • [19] On the use of SRIM for computing radiation damage exposure
    Stoller, R. E.
    Toloczko, M. B.
    Was, G. S.
    Certain, A. G.
    Dwaraknath, S.
    Garner, F. A.
    [J]. NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 2013, 310 : 75 - 80
  • [20] EBSD characterization of pure and K -doped tungsten fibers annealed at different temperatures
    Tanure, L.
    Terentyev, D.
    Nikolic, V.
    Riesch, J.
    Verbeken, K.
    [J]. JOURNAL OF NUCLEAR MATERIALS, 2020, 537
123