Bond Strength to Uthium-Disilicate Ceramic after Different Surface weaning Approaches

Purpose: To evaluate the effect of different lithium-disilicate (LiSi) glass-ceramic surface decontamination procedures on the shear bond strength (SBS) to resin cement Materials and Methods: Seventy CAD/CAM LiSi ceramic specimens (IPS e.max CAD, Ivoclar) were cut and sintered. Fifty specimens were treated with 5% hydrofluoric acid (HF) for 20 s, while 20 were left untreated. All 70 specimens were then contaminated with human saliva and try-in silicone paste. The following surface cleaning methods were investigated (n =10): C: water rinsing (control); PA: 37%H3PO4 etching for 20 s; E: 70%ethanol applied for 20 s; CP: cleaning paste (Ivoclean, Ivoclar) brushed for 20 s; HFSEP: self-etching ceramic primer (Monobond Etch&Prime, Ivoclar) rubbed for 20 s; HF: 5% HF applied for 20 s or no HF etching prior to contamination; SEP: self-etching ceramic primer rubbed for 20 s and no HF etching prior to contamination. Composite cylinders were created and luted with an adhesive resin cement to the decontaminated surfaces. After storage for 24h at 37(degrees)C, the SBS test was conducted. Two fractured specimens per group were observed under SEM to perform fractographic analysis. The data were statistically analyzed with p set at <0.05. Results: The type of surface cleaning approach influenced bond strength (p <0.001). HFSEP, SEP, and HF attained higher SBS (p <0.001) compared to other groups. None of the approaches were able to completely remove contaminants from the ceramic surfaces. SEM images showed residual traces of contaminants on CP-treated surfaces. Conclusions: The self-etching ceramic primer enhanced bond strength to contaminated LiSi ceramic surfaces, irrespective of previous treatment with hydrofluoric acid.