Effect of Al/Mn ratio on corrosion behavior of lean Mg-Zn-Ca-Al-Mn alloy processed by twin-roll casting

被引：19

作者：

Wang, Bing-Yu ^{[1
]}

Li, Mei-Xuan ^{[1
]}

Li, Yi-Jia ^{[1
]}

Wang, Yu-Fei ^{[1
]}

Gao, Yipeng ^{[1
]}

Wang, Hui-Yuan ^{[1
,2
]}

机构：

[1] Jilin Univ, Sch Mat Sci & Engn, Key Lab Automobile Mat, Minist Educ, 5988 Renmin St,Nanling Campus, Changchun 130025, Peoples R China

[2] Jilin Univ, Int Ctr Future Sci, Changchun 130012, Peoples R China

来源：

CORROSION SCIENCE | 2023年 / 212卷

基金：

中国国家自然科学基金;

关键词：

A; Magnesium; Alloy; intermetallics; C; passive films; Pitting corrosion; MAGNESIUM ALLOY; ELECTROCHEMICAL CORROSION; MECHANICAL-PROPERTIES; MICROSTRUCTURE; PHASE; REFINEMENT; EXTRUSION; MANGANESE; ADDITIONS; AZ31;

D O I：

10.1016/j.corsci.2022.110938

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Adopting twin-roll casting (TRC) technique, lean Mg-1.2Zn-0.3Ca-0.3Al-xMn (x = 0.25, 0.38, 0.5 wt%) alloys with different Al/Mn ratio were prepared. The stoichiometric ratio of Al8Mn5 is taken as dividing line. Under Al/ Mn>1.6, rhombohedral Al8Mn5 is formed, while under Al/Mn <= 1.6, cubic beta-Mn is generated. Because of lower Volta potential of Al8Mn5 than beta-Mn, the alloy with Al/Mn>1.6 shows the lowest average corrosion rate (4.55 mm y-1). The formation of fine rather than coarse Al8Mn5 weakens micro-galvanic corrosion and relieves stress concentration, thus simultaneously endowing the alloy (Al/Mn>1.6) with admirable corrosion resistance and mechanical properties (UTS:-266 MPa, YS:-193 MPa, EF:-20 %).

引用

页数：16

共 50 条

[41] Strengthening of Mg-Al-Zn-Mn alloy using SiC/Al nanocomposite extrusion
Emadi, P.
Andilab, B.
Borodianskiy, K.
Ravindran, C.
[J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2022, 922
[42] MICROSTRUCTURE AND MECHANICAL PROPERTIES OF Mg-12Zn-4Al-0.3Mn ALLOY CONTAINING Sr AND Ca
Wan Xiaofeng
Sun Yangshan
Xue Feng
Bai Jing
Tao Weijian
[J]. ACTA METALLURGICA SINICA, 2009, 45 (05) : 585 - 591
[43] Influence of Mn and Zr on the Corrosion of Al-Free Mg Alloys: Part 2-Impact of Mn and Zr on Mg Alloy Electrochemistry and Corrosion
Gandel, D. S.
Easton, M. A.
Gibson, M. A.
Birbilis, N.
[J]. CORROSION, 2013, 69 (08) : 744 - 751
[44] Effect of alloyed Sr on the microstructure and corrosion behavior of biodegradable Mg-Zn-Mn alloy in Hanks' solution
Pan, Hui
Pang, Kun
Cui, Fengzhen
Ge, Feng
Man, Cheng
Wang, Xin
Cui, Zhongyu
[J]. CORROSION SCIENCE, 2019, 157 : 420 - 437
[45] The influence of hot extrusion deformation on microstructure evolution, tensile properties and corrosion behavior of Mg-3Al-0.5Mn-0.5Sr alloy
Shen, Xia
Xu, Tiancai
Li, Boxin
[J]. MATERIALS EXPRESS, 2020, 10 (03) : 325 - 336
[46] Microstructure and Wear Properties of Al 7075 Alloy Manufactured by Twin-Roll Strip Casting Process
Kim, Kyoung-Wook
Baek, Min-Seok
Euh, Kwangjun
Lee, Kee-Ahn
[J]. KOREAN JOURNAL OF METALS AND MATERIALS, 2021, 59 (12): : 870 - 879
[47] Two-stage homogenization of Al-Zn-Mg-Cu-Zr alloy processed by twin-roll casting to improve L12 Al3Zr precipitation, recrystallization resistance, and performance
Li, Yong
Lu, Bing
Yu, Wei
Fu, Jinyu
Xu, Guangming
Wang, Zhaodong
[J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2021, 882
[48] Effect of Mn on Microstructure and Properties of Twin-Roll Casted 6061 Aluminum Alloy Plate
Wang Hongbin
Zhang Xinyu
Li Shengli
Xu Zhen
Song Hua
Lian Fabo
Chen Xingyu
[J]. RARE METAL MATERIALS AND ENGINEERING, 2021, 50 (01) : 129 - 137
[49] Role of alloyed Al on the microstructure and corrosion behavior of as-cast dilute Mg-2Zn-xAl-0.5Ca alloys
Li, Yi-Jia
Li, Mei-Xuan
Hua, Zhen-Ming
Wang, Bing-Yu
Gao, Yipeng
Wang, Hui-Yuan
[J]. CORROSION SCIENCE, 2023, 211
[50] Improvement of strength and ductility synergy in a room-temperature stretch-formable Mg-Al-Mn alloy sheet by twin-roll casting and low-temperature annealing
Nakata, T.
Xu, C.
Kaibe, K.
Yoshida, Y.
Yoshida, K.
Kamado, S.
[J]. JOURNAL OF MAGNESIUM AND ALLOYS, 2022, 10 (04) : 1066 - 1074

← 1 2 3 4 5 →